Superconductivity in CeBeH$_{8}$ and CeBH$_{8}$ at moderate pressures

Yu Hou; Bin Li; Yan Bai; Xiaofeng Hao; Yeqian Yang; Fengfeng Chi; Shengli Liu; Jie Cheng; Zhixiang Shi

doi:10.1088/1361-648X/ac9bbc

← Back to search

Superconductivity in CeBeH$_{8}$ and CeBH$_{8}$ at moderate pressures

Yu Hou, Bin Li, Yan Bai, Xiaofeng Hao, Yeqian Yang, Fengfeng Chi, Shengli Liu, Jie Cheng, Zhixiang Shi

arXiv:2210.17005 · DOI 10.1088/1361-648X/ac9bbc · 2022-10-31 · Journal of Physics: Condensed Matter

T1experimental4 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

High-pressure structural searches of superhydrides CeBeH$_8$ and CeBH$_8$ were performed under ambient pressure up to 300 GPa. We identify $Fm\overline{3}m$-CeBeH$_8$ with a superconducting transition temperature $T_{c}$ of 56 K at 10 GPa. Two more phases with spacegroup $R\overline{3}m$ and $C2/m$, were investigated within the increasing pressures. CeBH$_8$ shows a similar phase transition process as CeBeH$_8$ but with higher transition pressures and higher $T_c$. $Fm\overline{3}m$-CeBH$_8$ is predicted to be superconducting above 120 GPa with a maximum $T_{c}$ of 118 K at 150 GPa. $R\overline{3}m$-CeBH$_8$ and $C2/m$-CeBH$_8$ are dynamically stable above 120 GPa and 100 GPa, respectively. The maximum $T_{c}$ is 123 K at 195 GPa for $R\overline{3}m$-CeBH$_8$, and 115 K at 350 GPa for $C2/m$-CeBH$_8$. Our work enriches the family of ternary hydrides and may provide a useful guideline for further search for superconducting hydrides at low and moderate pressures.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
CeBeH8 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	56	10 GPa	unknown
CeBH8 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	118	150 GPa	unknown
CeBH8 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	123	195 GPa	unknown
CeBH8 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	115	350 GPa	unknown
H3S Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	203	Pressure not reported	unknown
LaH10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	260	Pressure not reported	unknown
CaYH12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	258	200 GPa	unknown
LiPH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	150	200 GPa	unknown
Li2MgH16 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	473	250 GPa	unknown
LaBH8 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	126	50 GPa	unknown
LaBH8 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	185	20 GPa	unknown