Orientation-dependent electron-phonon coupling in interfacial superconductors LaAlO3/KTaO3

Xiaoyang Chen; Tianlun Yu; Yuan Liu; Yanqiu Sun; Minyinan Lei; Nan Guo; Yu Fan; Xingtian Sun; Meng Zhang; Fatima Alarab; Vladimir N. Strokov; Yilin Wang; Tao Zhou; Xinyi Liu; Fanjin Lu; Weitao Liu; Yanwu Xie; Rui Peng; Haichao Xu; Donglai Feng

doi:10.1038/s41467-024-51969-4

Orientation-dependent electron-phonon coupling in interfacial superconductors LaAlO3/KTaO3

Xiaoyang Chen, Tianlun Yu, Yuan Liu, Yanqiu Sun, Minyinan Lei, Nan Guo, Yu Fan, Xingtian Sun, Meng Zhang, Fatima Alarab, Vladimir N. Strokov, Yilin Wang, Tao Zhou, Xinyi Liu, Fanjin Lu, Weitao Liu, Yanwu Xie, Rui Peng, Haichao Xu, Donglai Feng

arXiv:2301.13488 · DOI 10.1038/s41467-024-51969-4 · 2023-01-31 · Nature Communications

T3experimental31 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The emergent superconductivity at the LaAlO3/KTaO3 interfaces exhibits a mysterious dependence on the KTaO3 crystallographic orientations. Here we show, by soft X-ray angle-resolved photoemission spectroscopy, that the interfacial superconductivity is contributed by mobile electrons with unexpected quasi-three-dimensional character, beyond the "two-dimensional electron gas" scenario in describing oxide interfaces. At differently-oriented interfaces, the quasi-three-dimensional electron gas ubiquitously exists and spatially overlaps with the small q Fuchs-Kliewer surface phonons. Intriguingly, electrons and the Fuchs-Kliewer phonons couple with different strengths depending on the interfacial orientations, and the stronger coupling correlates with the higher superconducting transition temperature. Our results provide a natural explanation for the orientation-dependent superconductivity, and the first evidence that interfacial orientations can affect electron-phonon coupling strength over several nanometers, which may have profound implications for the applications of oxide interfaces in general.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaAlO3/SrTiO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.2	Pressure not reported	unknown
LaAlO3/KTaO3(111) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2	Pressure not reported	unknown
LaAlO3/KTaO3(110) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.9	Pressure not reported	unknown