Superconducting TSV contact for cryoelectronic devices
Filippov, Ivan, Anikanov, Alexandr, Rykov, Aleksandr, Mumlyakov, Alexander, Shibalov, Maksim, Trofimov, Igor, Porokhov, Nikolay, Anufriev, Yuriy, Tarkhov, Michael
arXiv:2308.06000 · 2023-08-14
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
This work focuses on the fabrication of niobium through silicon vias (TSV) superconductors interconnects. The effect of supercycle of sequential oxidation and chemical etching process on the through-etch wall quality was investigated. It was experimentally shown that the use of supercycle in the fabrication process leads to significant improvement of the TSV wall quality and removal of the defect type - scallops. After 12 times repetitions of supercycles a dissipative bonding of superconducting strips on the front and back side of the sample is observed. The critical current density of such coupling is 5x104 A/cm2. The critical ratio of substrate thickness to hole diameter at which electrical coupling is formed is 3 : 1.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Nb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Fabrication of superconducting through-silicon vias
similarity 0.84Justin L. Mallek et al. · 2021 · arXiv:2103.08536
Source status unknown — claims are unverified
3D integration and packaging for solid-state qubits
similarity 0.82D. Rosenberg et al. · 2019 · arXiv:1906.11146
Source status unknown — claims are unverified
Large grain boundary area superconductors
similarity 0.82G. Hammerl et al. · 2002 · arXiv:cond-mat/0207027
Source status unknown — claims are unverified
Superconductivity of interface layer at contact between normal metal and high temperature superconductor
similarity 0.82Oleg P. Ledenyov & Valery A. Frolov · 2013 · arXiv:1301.5542
Source status unknown — claims are unverified
Developments Toward a 250-nm, Fully Planarized Fabrication Process With Ten Superconducting Layers And Self-Shunted Josephson Junctions
similarity 0.81Sergey K. Tolpygo et al. · 2017 · arXiv:1704.07683
Source status unknown — claims are unverified
Signatures of Majorana Bound States in the Diffraction Patterns of Extended Superconductor-Topological Insulator-Superconductor Josephson Junctions
similarity 0.81Guang Yue et al. · 2023 · arXiv:2311.16489
Source status unknown — claims are unverified