Superconductivity in the cobalt-doped V3Si A15 intermetallic compound

Zeng, Lingyong; Zhou, Huawei; Du, Hong; Zhong, Ruidan; Guo, Ruixin; Guo, Shu; Su, Wanzhen; Li, Kuan; Zhang, Chao; Yu, Peifeng; Luo, Huixia

Superconductivity in the cobalt-doped V3Si A15 intermetallic compound

Zeng, Lingyong, Zhou, Huawei, Du, Hong, Zhong, Ruidan, Guo, Ruixin, Guo, Shu, Su, Wanzhen, Li, Kuan, Zhang, Chao, Yu, Peifeng, Luo, Huixia

arXiv:2309.11055 · 2023-09-21

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The A15 structure of superconductors is a prototypical type-II superconductor that has generated considerable interest since the early history of superconducting materials. This paper discusses the superconducting properties of previously unreported V3-xCoxSi alloys. It is found that the lattice parameter decreases with increasing cobalt-doped content and leads to an increased residual resistivity ratio (RRR) value of the V3-xCoxSi system. Meanwhile, the superconducting transition temperature (Tc) cobalt-doped content. Furthermore, the fitted data show that the increase of cobalt-doped content also reduces the lower/upper critical fields of the V3-xCoxSi system. Type-II superconductivity is demonstrated on all V3-xCoxSi samples. With higher Co-doped content, V3-xCoxSi alloys may have superconducting and structural phase transitions at low-temperature regions. As the electron/atom (e/a) ratio increases, the Tc variation trend of V3Si is as pronounced as in crystalline alloys and monotonically follows the trend observed for amorphous superconductors.