Diboride compounds doped with transition metals$\unicode{x2013}$a route to superconductivity through structure stabilization as well as defects
P. M. Dee, J. S. Kim, A. C. Hire, J. Lim, L. Fanfarillo, S. Sinha, J. J. Hamlin, R. G. Hennig, P. J. Hirschfeld, G. R. Stewart
arXiv:2310.03818 · DOI 10.1103/PhysRevB.109.104520 · 2023-10-05 · Physical Review B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Recent investigations into MoB$_{2}$ have unveiled a direct connection between a pressure-induced structural transition to a P6/mmm space group structure and the emergence of superconductivity, producing critical temperatures up to 32 K at 100 GPa. This pressure-induced superconducting state underscores the potential of doped MoB$_{2}$ as a possible candidate for metastable superconductivity at ambient pressure. In this work, we demonstrate that doping by Zr, Hf, or Ta stabilizes the P6/mmm structure at ambient pressure and results in the realization of a superconducting state with critical temperatures ranging from 2.4 up to 8.5 K depending on the specific doping. We estimate the electron-phonon coupling $λ$ and the density of states based on resistivity and specific heat data, finding that $λ$ ranges from 0.4 - 0.6 for these compounds. Finally, to investigate the role of possible metastable defect structures on the critical temperature, we analyze MoB$_{2}$, MoB$_{2.5}$, and Nb/Zr-doped MoB$_{2}$ using rapid cooling techniques. Notably, splat-quenching produces samples with higher critical temperatures and even retains superconductivity in MoB$_{2}$ at ambient pressure, achieving a critical temperature of 4.5 K.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 32 | 100 GPa | unknown |
| MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 4.5 | Pressure unresolved | unknown |
| MoB2.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.1 | Pressure unresolved | unknown |
| MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 4.45 | Pressure unresolved | onset |
| MoB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 4.55 | Pressure unresolved | onset |
| MoB2.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 3.06 | Pressure unresolved | onset |
| MoB2.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 5.82 | Pressure unresolved | onset |
| MoB2.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 2.88 | Pressure unresolved | unknown |
| (Zr0.04Mo0.96)0.85B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.6 | Pressure unresolved | onset |
| (Zr0.04Mo0.96)0.85B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.65 | Pressure unresolved | midpoint |
| (Zr0.04Mo0.96)0.85B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 10.14 | Pressure unresolved | onset |
| (Zr0.04Mo0.96)0.85B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.6 | Pressure unresolved | onset |
| (Zr0.04Mo0.96)0.85B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.09 | Pressure unresolved | midpoint |
| Nb0.25Mo0.75B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.05 | Pressure unresolved | onset |
| Nb0.25Mo0.75B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 10.45 | Pressure unresolved | onset |
| Nb0.25Mo0.75B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 10.67 | Pressure unresolved | onset |
| (Zr0.04Mo0.96)0.85B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.137 | Pressure unresolved | onset |
| (Hf0.04Mo0.96)0.85B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.45 | Pressure unresolved | onset |
| (Hf0.04Mo0.96)0.85B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.27 | Pressure unresolved | midpoint |
| (Hf0.04Mo0.96)0.80B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8 | Pressure unresolved | onset |
| (Nb0.95Mo0.05)0.80B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 3.5 | Pressure unresolved | onset |
| (Ti0.04Mo0.96)0.80B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 5 | Pressure unresolved | onset |
| (Ti0.04Mo0.96)0.80B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.4 | Pressure unresolved | onset |
| (Ti0.04Mo0.96)0.80B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7 | Pressure unresolved | midpoint |
| (Sc0.05Mo0.95)0.83B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 6.01 | Pressure unresolved | onset |
Similar papers
Dissipation by surface states in superconducting RF cavities
similarity 0.95Sean Deyo et al. · 2022 · arXiv:2201.07747
Source status unknown — claims are unverified
Thermal annealing of sputtered Nb3Sn and V3Si thin films for superconducting radio-frequency cavities
similarity 0.95Katrina Howard et al. · 2023 · arXiv:2301.00756
Source status unknown — claims are unverified
In-situ scattering studies of superconducting vacancy-ordered monoclinic TiO thin films
similarity 0.93Merve Baksi et al. · 2023 · arXiv:2305.16973
Source status unknown — claims are unverified
Elastocaloric evidence for a multicomponent superconductor stabilized within the nematic state in Ba(FeCo)As
similarity 0.92Sayak Ghosh et al. · 2024 · arXiv:2402.17945
Source status unknown — claims are unverified
Superconducting Phase of Thin Films Grown by Molecular Beam Epitaxy
similarity 0.92Yasemin Ozbek et al. · 2022 · arXiv:2203.01405
Source status unknown — claims are unverified
Field-angle evolution of the superconducting and magnetic phases of UTe around the axis
similarity 0.92Sylvia K. Lewin et al. · 2024 · arXiv:2410.05137
Source status unknown — claims are unverified