Effect of annealing in eutectic high-entropy alloy superconductor NbScTiZr
Takeru Seki, Hiroto Arima, Yuta Kawasaki, Terukazu Nishizaki, Yoshikazu Mizuguchi, Jiro Kitagawa
arXiv:2311.00195 · DOI 10.1007/s10948-023-06643-z · 2023-11-01 · Journal of Superconductivity and Novel Magnetism
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We investigated the impact of annealing on the structural characteristics and superconducting critical temperature ($T_\mathrm{c}$) of the eutectic high-entropy alloy (HEA) superconductor NbScTiZr. The HEA manifests an eutectic microstructure composed of body-centered cubic (bcc) and hexagonal close-packed phases. Both the lattice parameters of the bcc phase and grain size of the eutectic structure exhibited pronounced sensitivity to variations in annealing temperature. The observed dependence of the lattice parameter on annealing temperature supports the possibility that lattice strain occurs at lower annealing temperatures. The as-cast sample demonstrated superconductivity at $T_\mathrm{c}$ of 7.9 K, which increased to 9 K after annealing at 800 $^{\circ}$C. However, when subjected to annealing at 1000 $^{\circ}$C, $T_\mathrm{c}$ diminishes to 8.7 K. The annealing-temperature dependence of $T_\mathrm{c}$ cannot be comprehensively elucidated based solely on the electronic density of states at the Fermi level. It is plausible that the lattice strain may influence the annealing temperature dependence of $T_\mathrm{c}$. Our results for the critical current density $J_{c}$ reveal that the self-field $J_{c}$ of the as-cast NbScTiZr at 2 K exceeds 10$^{6}$ A/cm$^{2}$.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| NbScTiZr Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.9 | Pressure not reported | unknown |
| NbScTiZr Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.9 | Pressure not reported | unknown |
| NbScTiZr Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.4 | Pressure not reported | unknown |
| NbScTiZr Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.4 | Pressure not reported | unknown |
| NbScTiZr Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9 | Pressure not reported | unknown |
| NbScTiZr Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9 | Pressure not reported | unknown |
| NbScTiZr Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.7 | Pressure not reported | unknown |
| NbScTiZr Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.7 | Pressure not reported | unknown |
| (TaNb)0.67(HfZrTi)0.33 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8 | 180 GPa | unknown |
| Sr2RuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 1.5 | Pressure not reported | unknown |
| Ir Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 0.1 | Pressure not reported | unknown |
| Zr5Pt3O0.6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 3.2 | Pressure not reported | unknown |
| Zr5Pt3O2.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 4.8 | Pressure not reported | unknown |
| NbScTiZr Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 7.3 | Pressure not reported | unknown |
Similar papers
Electronic and magnetic properties of LaCuSb tuned by Cu occupancy
similarity 0.93Suyoung Kim et al. · 2024 · arXiv:2410.14909
Source status unknown — claims are unverified
Superconductivity in Al-Nb-Ti-V-Zr multicomponent alloy
similarity 0.91Yuta Harayama & Jiro Kitagawa · 2021 · arXiv:2107.09187
Source status unknown — claims are unverified
Coexistence of ferromagnetism and superconductivity at KTaO heterointerfaces
similarity 0.91Zhongfeng Ning et al. · 2023 · arXiv:2302.01549
Source status unknown — claims are unverified
A possible explanation for the high superconducting Tc in bcc Ti at high pressure
similarity 0.90Antonio Sanna et al. · 2023 · arXiv:2308.14672
Source status unknown — claims are unverified
Metallurgy, superconductivity, and hardness of a new high-entropy alloy superconductor Ti-Hf-Nb-Ta-Re
similarity 0.90Takuma Hattori et al. · 2023 · arXiv:2307.01958
Source status unknown — claims are unverified
New high-entropy alloy superconductor HfNbTiVZr
similarity 0.90Naoki Ishizu & Jiro Kitagawa · 2019 · arXiv:1904.03291
Source status unknown — claims are unverified