Superconductivity above 180 K in Ca-Mg Ternary Superhydrides at Megabar Pressures
Cai, Weizhao, Minkov, Vasily S., Sun, Ying, Kong, Panpan, Sawchuk, Krista, Maiorov, Boris, Balakirev, Fedor F., Chariton, Stella, Prakapenka, Vitali B., Ma, Yanming, Eremets, Mikhail I.
arXiv:2312.06090 · 2023-12-12
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The discovery of high-temperature superconductivity above 240 K in binary La-H and Y-H systems inspired further predictions of even higher transition temperatures in compounds such as YH10 and MgH6, which are likely to be dynamically unstable. Ternary superhydrides provide alternative pathways to stabilize desired near-room temperature superconducting phases. However, the synthesis of new ternary hydrides remains challenging because most of the precursor reactants do not exist in desired stoichiometry at ambient conditions. Here we report that using the existing binary intermetallic CaMg2 and 1:1 Ca-Mg mixture as starting reactants, we have successfully synthesized novel Ca-Mg-based ternary superhydrides at megabar pressures. Electrical resistivity measurements show Tc approaching 168 K at 310 GPa in the CaMg2-based superhydride and 182 K in 1:1 the Ca-Mg superhydride at 324 GPa.
Similar papers
Superconductivity above 200 K Observed in Superhydrides of Calcium
similarity 0.92Z. Li et al. · 2021 · arXiv:2103.16917
Source status unknown — claims are unverified
Phase diagrams and superconductivity of ternary Ca-Al-H compounds under high pressure
similarity 0.91Ming Xu et al. · 2023 · arXiv:2305.11678
Source status unknown — claims are unverified
Pressure-induced high−Tc superconductivity in the ternary clathrate system Y-Ca-H
similarity 0.90Wendi Zhao et al.
Source status unknown — claims are unverified
High-temperature Superconductivity in Perovskite Hydride below 10 GPa
similarity 0.90Mingyang Du et al. · 2024 · arXiv:2407.03556
Source status unknown — claims are unverified
Stoichiometric Ternary Superhydride LaBeH8 as a New Template for High-Temperature Superconductivity at 110 K under 80 GPa
similarity 0.90Yinggang Song et al.
Source status unknown — claims are unverified
High-temperature superconductivity below 100 GPa in ternary C-based hydride MC2H8 with molecular crystal characteristics (M= Na, K, Mg, Al, and Ga)
similarity 0.90Meng-Jing Jiang et al.
Source status unknown — claims are unverified