Superconductivity above 200 K Observed in Superhydrides of Calcium
Z. Li, X. He, C. L. Zhang, X. C. Wang, S. J. Zhang, Y. T. Jia, S. M. Feng, K. Lu, J. F. Zhao, J. Zhang, B. S. Min, Y. W. Long, R. C. Yu, L. H. Wang, M. Y. Ye, Z. S. Zhang, V. Prakapenka, S. Chariton, P. A. Ginsberg, J. Bass, S. H. Yuan, H. Z. Liu, C. Q. Jin
arXiv:2103.16917 · DOI 10.1038/s41467-022-30454-w · 2021-03-31 · Nature Communications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Searching for superconductivity with Tc near room temperature is of great interest both for fundamental science & many potential applications. Here we report the experimental discovery of superconductivity with maximum critical temperature (Tc) above 210 K in calcium superhydrides, the new alkali earth hydrides experimentally showing superconductivity above 200 K in addition to sulfur hydride & rare-earth hydride system. The materials are synthesized at the synergetic conditions of 160~190 GPa and ~2000 K using diamond anvil cell combined with in-situ laser heating technique. The superconductivity was studied through in-situ high pressure electric conductance measurements in an applied magnetic field for the sample quenched from high temperature while maintained at high pressures. The upper critical field Hc(0) was estimated to be ~268 T while the GL coherent length is ~11 angstrom. The in-situ synchrotron X-ray diffraction measurements suggest that the synthesized calcium hydrides are primarily composed of CaH6 while there may also exist other calcium hydrides with different hydrogen contents.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| CaH6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 210 | 160 GPa | unknown |
Similar papers
High-Temperature Superconducting Phase in Clathrate Calcium Hydride CaH6 up to 215 K at a Pressure of 172 GPa
similarity 0.94Liang Ma et al.
Source status unknown — claims are unverified
High-Tc superconductivity in clathrate calcium hydride CaH6
similarity 0.94Liang Ma et al. · 2021 · arXiv:2103.16282
Source status unknown — claims are unverified
Superconductivity above 180 K in Ca-Mg Ternary Superhydrides at Megabar Pressures
similarity 0.92Cai, Weizhao et al. · 2023 · arXiv:2312.06090
Source status unknown — claims are unverified
Revisiting Phase Stability and Superconductivity in Ca-H Superhydrides with Anharmonic Effects
similarity 0.90Wenbo Zhao et al. · 2025 · arXiv:2512.03721
Source status unknown — claims are unverified
Superconductivity at 215 K in lanthanum hydride at high pressures
similarity 0.90A. P. Drozdov et al. · 2018 · arXiv:1808.07039
Source status unknown — claims are unverified
Superconductivity in Zirconium Polyhydrides with Tc above 70 K
similarity 0.90C. L. Zhang et al. · 2021 · arXiv:2112.14439
Source status unknown — claims are unverified