Effects of Li Doping on Superconducting Properties of Citrate Gel Prepared Y1-xLixBa2Cu3O7-d Compound
Mahshid Amiri Moghadam, Hassan Gashmard, Seyed Sajjad Hosseini, Hamideh Shakeripour, Hadi Salamati
arXiv:2401.03471 · DOI 10.1007/s00339-022-06162-z · 2024-01-07
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The Y1-xLixBa2Cu3O7-d polycrystalline bulk superconductors doped with Li substituting at the Y site at different concentrations (x = 0, 0.01, 0.02, 0.1) were prepared using the citrate-gel method to study the effects of doping on the superconducting temperature and critical current density. The question was whether Li addition characterized by a high Debye frequency would have any positive effects on Tc. The optimum citrate-gel and heat treatment conditions were identified as those yielding samples with a maximum grain size on the order of 50 micro.m (up to the optimum Li-doping level, x=0.01). Li substitution at the Y site was verified by structural, electrical, and magnetic measurements of the produced samples, whereas X-ray diffraction (XRD) analysis revealed the formation of a pure phase with no visible impurity phases. Moreover, AC magnetic susceptibility measurements showed no increase in the superconducting transition temperature Tc, consistent with the predicted results obtained by machine learning method, although it was theoretically expected to increase owing to the high Debye frequency of Li. This observation is consistent with magnetic coupling models for pairing mechanism in cuprates. Finally, because of the optimum conditions of the preparation procedure, nearly identical values of the critical current density (Jc) were recorded for samples with different Li doping levels (up to the optimum Li doping level). It was found that improved compound preparation conditions would have a critical and extensive effect on Jc enhancement, with nearly no Tc suppression.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Y1-xLixBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Synthesis and superconducting properties of Y(Ba1−yLay)2Cu4O8 and (Y1−xCax)(Ba1−yLay)2Cu4O8
similarity 0.87Takeshi Sakurai et al.
Source status unknown — claims are unverified
Effect of Li doping on structure and superconducting transition temperature of Mg1-xLixB2
similarity 0.86Y. G. Zhao et al. · 2001 · arXiv:cond-mat/0103077
Source status unknown — claims are unverified
Enhancement in transition temperature and critical current density of CeO0.8F0.2FeAs by yttrium doping
similarity 0.86J. Prakash et al. · 2009 · arXiv:0908.3372
Source status unknown — claims are unverified
MgB2 single crystals substituted with Li and with Li-C: Structural and superconducting properties
similarity 0.86J. Karpinski et al.
Source status unknown — claims are unverified
Revival of Superconductivity by Y3+/Ca2+ substitution in YBa2Cu2.7Co0.3O7 without reported phase transformation
similarity 0.86M. A. Ansari et al. · 2004 · arXiv:cond-mat/0412152
Source status unknown — claims are unverified
The role of Ca in superconducting and magnetic properties of Y1-xCaxBa2Cu3O7 (x = 0.0-0.30)
similarity 0.85N. P. Liyanawaduge et al. · 2011 · arXiv:1106.3144
Source status unknown — claims are unverified