Enhanced Superconductivity in SrTiO$_3$-based Interfaces via Amorphous Al2O3 Capping

I. Silber; A. Azulay; A. Basha; D. Ketchker; M. Baskin; A. Yagoda; L. Kornblum; A. Kohn; Y. Dagan

← Back to search

Enhanced Superconductivity in SrTiO$_3$-based Interfaces via Amorphous Al2O3 Capping

I. Silber, A. Azulay, A. Basha, D. Ketchker, M. Baskin, A. Yagoda, L. Kornblum, A. Kohn, Y. Dagan

arXiv:2402.14051 · 2024-02-21

T31 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Oxide interfaces feature unique two-dimensional (2D) electronic systems with diverse electronic properties such as tunable spin-orbit interaction and superconductivity. Conductivity emerges in these interfaces when the thickness of an epitaxial polar layer surpasses a critical value, leading to charge transfer to the interface. Here, we show that depositing amorphous alumina on top of the polar oxide can reduce the critical thickness and enhance the superconducting properties for the (111) and the (100) SrTiO$_3$-based interfaces. A detailed transmission electron microscopy analysis reveals that the enhancement of the superconducting properties is linked to the expansion of the LaAlO$_3$ lattice in a direction perpendicular to the interface. We propose that the increase in the superconducting critical temperature, Tc, is a result of epitaxial strain

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
SrTiO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.42	Pressure not reported	unknown
SrTiO3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.365	Pressure not reported	unknown