High-temperature Superconducting Oxide without Copper at Ambient Pressure

S. Lin Er Chow; Zhaoyang Luo; A. Ariando

High-temperature Superconducting Oxide without Copper at Ambient Pressure

S. Lin Er Chow, Zhaoyang Luo, A. Ariando

arXiv:2410.00144 · 2024-09-30

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The discovery of superconductivity in the Ba-La-Cu-O system (the cuprate) at the 30 K range in 1986 marked a significant breakthrough, as it far exceeded the highest known critical temperature ($T_c$) at the time and surpassed the predicted 30 K limit, which was thought to be the maximum before phonon-mediated electron pairing would break down due to thermal excitation. Despite recent successful observations of superconductivity in nickel-oxide-based compounds (the nickelate), superconductivity above 30 K at ambient pressure in a system that is isostructural and isoelectronic to the cuprate but without copper has remained elusive. Here, we report a superconducting $T_c$ above 35 K under ambient pressure in hole-doped, late rare-earth infinite-layer nickel oxide (Sm-Eu-Ca-Sr)NiO$_2$ thin films. Electron microscopy reveals a small thickness of ~2 nm of infinite-layer phase stabilised at present, which indicates a higher temperature superconductivity should be observable in clean bulk crystals.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
(Sm-Eu-Ca-Sr)NiO2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	35	Pressure unresolved	onset