Thermal Annealing and Radiation Effects on Structural and Electrical Properties of NbN/GaN Superconductor/Semiconductor Junction

Stephen Margiotta; Binzhi Liu; Saleh Ahmed Khan; Gabriel Calderon Ortiz; Ahmed Ibreljic; Jinwoo Hwang; A F M Anhar Uddin Bhuiyan

doi:10.1116/6.0004539

Thermal Annealing and Radiation Effects on Structural and Electrical Properties of NbN/GaN Superconductor/Semiconductor Junction

Stephen Margiotta, Binzhi Liu, Saleh Ahmed Khan, Gabriel Calderon Ortiz, Ahmed Ibreljic, Jinwoo Hwang, A F M Anhar Uddin Bhuiyan

arXiv:2501.07780 · DOI 10.1116/6.0004539 · 2025-01-14 · Journal of Vacuum Science & Technology A

T1experimental1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

In the rapidly evolving field of quantum computing, niobium nitride (NbN) superconductors have emerged as integral components due to their unique structural properties, including a high superconducting transition temperature (Tc), exceptional electrical conductivity, and compatibility with advanced device architectures. This study investigates the impact of high-temperature annealing and high-dose gamma irradiation on the structural and superconducting properties of NbN films grown on GaN via reactive DC magnetron sputtering. The as-deposited cubic δ-NbN (111) films exhibited a high-intensity XRD peak, high Tc of 12.82K, and an atomically flat surface. Annealing at 500 and 950 °C for varying durations revealed notable structural and surface changes. High-resolution STEM indicated improved local ordering, while AFM showed reduced surface roughness after annealing. XPS revealed a gradual increase in the Nb/N ratio with higher annealing temperatures and durations. High-resolution XRD and STEM analyses showed lattice constant modifications in δ-NbN films, attributed to residual stress changes following annealing. Additionally, XRD phi-scans revealed sixfold symmetry in NbN films due to rotational domains relative to GaN. While Tc remained stable after annealing at 500 °C, increasing the annealing temperature to 950 °C degraded Tc to ~8K and reduced the residual resistivity ratio from 0.85 in as-deposited films to 0.29 after 30 minutes. The effects of gamma radiation (5 Mrad (Si)) were also studied, demonstrating minimal changes to crystallinity and superconducting performance, indicating excellent radiation resilience. These findings highlight the potential of NbN superconductors for integration into advanced quantum devices and their suitability for applications in radiation-intensive environments such as space, satellites, and nuclear power plants.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
NbN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	12.82	Pressure not reported	unknown
NbN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	12.82	Pressure not reported	unknown
NbN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure not reported	unknown
NbN Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	12.82	Pressure not reported	unknown