Pressure-induced structural and superconducting transitions in black arsenic

Wu, Y. Y.; Mu, L.; Zhang, Y. L.; Dai, D. Z.; Meng, K.; Huang, S. Y.; Zhang, X.; Huang, S. C.; Chen, J.; Yan, H. G.; Li, S. Y.

Pressure-induced structural and superconducting transitions in black arsenic

Wu, Y. Y., Mu, L., Zhang, Y. L., Dai, D. Z., Meng, K., Huang, S. Y., Zhang, X., Huang, S. C., Chen, J., Yan, H. G., Li, S. Y.

arXiv:2502.01955 · 2025-02-05

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report high-pressure Raman spectra and resistance measurements of black arsenic (b-As) up to 58 GPa, along with phonon density of states (DOS) and enthalpy calculations for four reported arsenic phases up to 50 GPa. It is found that metastable b-As transforms into gray arsenic (g-As) phase at a critical pressure of 1.51 GPa, followed by subsequent transitions to simple cubic arsenic (c-As) and incommensurate host-guest arsenic (hg-As) phases at 25.9 and 44.8 GPa, respectively. Superconductivity emerges above 25 GPa in the c-As phase, with the superconducting transition temperature ($T$$\rm_c$) remaining nearly a constant of 3 K. Upon further compression, $T$$\rm_c$ steeply increases to a higher value around 4.5 K in the incommensurate hg-As phase above 43 GPa. We use our results to update the structural and superconducting phase diagrams under pressure for the novel semiconductor, black arsenic.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
As Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3	25.4 GPa	onset
As Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.5	43 GPa	onset
As Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.05	10 GPa	unknown
As Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.7	24 GPa	unknown
As Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.5	32 GPa	unknown