Extremely high sensitivity to uniaxial stress in pressure induced superconductivity of BaFe2As2

Takehiro Yamazaki; Nao Takeshita; Ryosuke Kobayashi; Hideto Fukazawa; Yoh Kohori; Kunihiro Kihou; Chul-Ho Lee; Hijiri Kito; Akira Iyo; Hiroshi Eisaki

doi:10.1103/PhysRevB.81.224511

Extremely high sensitivity to uniaxial stress in pressure induced superconductivity of BaFe2As2

Takehiro Yamazaki, Nao Takeshita, Ryosuke Kobayashi, Hideto Fukazawa, Yoh Kohori, Kunihiro Kihou, Chul-Ho Lee, Hijiri Kito, Akira Iyo, Hiroshi Eisaki

arXiv:1003.0913 · DOI 10.1103/PhysRevB.81.224511 · 2010-03-03

T1experimental2 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We have performed electrical resistivity measurements on single crystal BaFe2As2 under high pressure P up to 16 GPa with a cubic anvil apparatus, and up to 3 GPa with a modified Bridgman anvil cell. The samples were obtained from the same batch, which was grown with a self-flux method. A cubic anvil apparatus provides highly hydrostatic pressure, and a modified Bridgman anvil cell, which contains liquid pressure transmitting medium, provides quasi hydrostatic pressure. For highly hydrostatic pressure, the crystal phase and magnetic transition temperature decreases robustly with P and disappears at around 10 GPa. The superconducting phase appears adjacent to magnetic phase in narrow pressure region between 11 and 14 GPa. The tiny difference of hydrostaticity between the cubic anvil apparatus and modified Bridgman anvil cell induces a drastic effect on the phase diagram of BaFe2As2. This result indicates that small uniaxial stress along c-axis strongly suppresses the structural/antiferromagnetic ordering and stabilizes superconductivity at much lower pressure.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
BaFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	17	11 GPa	onset
BaFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13	11.5 GPa	zero_resistance
LaFeAsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	unknown
BaFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38	Pressure not reported	unknown
Pb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown