Fabrication of oxide/FeSe multilayer films using the PLD technique
Tomoki Kobayashi, Hiroki Nakagawa, Ryo Ogawa, Atsutaka Maeda
arXiv:2509.23591 · DOI 10.1103/q829-ztzb · 2026-08-05
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
In this study, we demonstrate the successful fabrication of TiO2/FeSe/STO and TiO2/FeSe/LaAlO3 heterostructures using PLD. When the growth rates were sufficiently low, anatase TiO2, which has been reported to induce superconductivity in FeSe, could be grown epitaxially on FeSe. For TiO2/FeSe/STO, the FeSe/TiO2 interface was relatively clean, as confirmed by the observation of Laue fringes in FeSe(001) reflection. Although a thinner FeSe layer is expected to enhance Tc, our results instead suggest that deposition of TiO2 introduces additional disorder in FeSe. Most strikingly, superconductivity appeared when TiO2 was deposited on FeSe/LaAlO3, clearly demonstrating that the interaction between the top oxide layer and underlying FeSe can induce superconductivity. This work demonstrates the feasibility of fabricating FeSe/oxide superlattices by PLD, establishing a novel platform for the exploration of interfacial superconductivity in iron-based superconductors.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9 | Pressure unresolved | unknown |
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 46 | Pressure not reported | zero_resistance |
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 65 | Pressure not reported | onset |
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 40 | Pressure not reported | onset |
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 16 | Pressure not reported | onset |
Similar papers
Growth and characterization of high-quality FeSe thin films on SrTiO3 with enhanced superconductivity
similarity 0.92Zhanyi Zhao et al.
Source status unknown — claims are unverified
Electronic structure of FeSe monolayer superconductors
similarity 0.91I. A. Nekrasov et al. · 2016 · arXiv:1605.02404
Source status unknown — claims are unverified
Superconductivity in single-layer films of FeSe with a transition temperature above 100 K
similarity 0.90Jian-Feng Ge et al. · 2014 · arXiv:1406.3435
Source status unknown — claims are unverified
First-principles study of magnetic frustration in FeSe epitaxial films on SrTiO
similarity 0.90Kai Liu et al. · 2015 · arXiv:1501.03923
Source status unknown — claims are unverified
Interface induced high temperature superconductivity in single unit-cell FeSe films on SrTiO3
similarity 0.90Qing-Yan Wang et al. · 2012 · arXiv:1201.5694
Source status unknown — claims are unverified
Evolution of transport properties in FeSe thin flakes with thickness approaching the two-dimensional limit
similarity 0.90C. S. Zhu et al. · 2021 · arXiv:2107.10481
Source status unknown — claims are unverified