Microstructure of the highly dense MgB2 Superconductor by transmission electron microscope
Gun Yong Sung, Sang Hyeob Kim, JunHo Kim, Dong Chul Yoo, Ju Wook Lee, Jeong Yong Lee, C. U. Jung, Min-Seok Park, W. N. Kang, Du Zhonglian, Sung-Ik Lee
arXiv:cond-mat/0102498 · 2001-02-27 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of about 3 GPa was investigated by using a high-resolution transmission electron microscope (HRTEM). The TEM images did not show any pores in the specimen. All grains were compactly connected, and no discernable empty spaces or impurities at the boundaries existed over the regions investigated. The HRTEM image showed clearly each constituent atom that formed the basal hexagonal plane, without any defect in a single grain. The a-axis lattice parameter, 0.307 nm, from this direct measurement was shorter than the value, 0.314 nm obtained from samples prepared using diffusion techniques. A minor impurity phase, which was most probably MgB4 and did not form interfacial layers was also observed, but was well isolated from the main MgB2 phase. Our results verify that the MgB2 powder was sintered under high temperature and high pressure into its theoretical density without any porosity or grain growth.
Similar papers
Superconductivity in Dense Wires
similarity 0.90P. C. Canfield et al. · 2001 · arXiv:cond-mat/0102289
Source status unknown — claims are unverified
Effect of sintering temperature under high pressure in the uperconductivity for MgB2
similarity 0.90C. U. Jung et al. · 2001 · arXiv:cond-mat/0102383
Source status unknown — claims are unverified
Superconducting properties of nanocrystalline MgB thin films made by an in situ annealing process
similarity 0.89X. H. Zeng et al. · 2001 · arXiv:cond-mat/0105080
Source status unknown — claims are unverified
Compressibility of the MgB2 superconductor
similarity 0.89K. Prassides et al.
Source status unknown — claims are unverified
Compressibility of the MgB2 Superconductor
similarity 0.89K. Prassides et al. · 2001 · arXiv:cond-mat/0102507
Source status unknown — claims are unverified
Superconductivity in Dense MgB2 Wires
similarity 0.89P. C. Canfield et al.
Source status unknown — claims are unverified