C. U. Jung, Min-Seok Park, W. N. Kang, Mun-Seog Kim, Kijoon H. P. Kim, S. Y. Lee, Sung-Ik Lee
arXiv:cond-mat/0102383 · DOI 10.1063/1.1382632 · 2001-02-21 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report the effect of the sintering temperature on the superconductivity of MgB2 pellets prepared under a high pressure of 3 GPa. The superconducting properties of the non-heated MgB2 in this high pressure were poor. However, as the sintering temperature increased, the superconducting properties were vastly enhanced, which was shown by the narrow transition width for the resistivity and the low-field magnetizations. This shows that heat treatment under high pressure is essential to improve superconducting properties. These changes were found to be closely related to changes in the surface morphology observed using scanning electron microscopy.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 40 | 3 GPa | onset |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 40 | 3 GPa | onset |
Similar papers
Hole carrier in MgB_{2} characterized by Hall Measurements
similarity 0.90W. N. Kang et al. · 2001 · arXiv:cond-mat/0102313
Source status unknown — claims are unverified
Pressure dependent thermoelectric power of MgB superconductor
similarity 0.90E. S. Choi et al. · 2001 · arXiv:cond-mat/0104454
Source status unknown — claims are unverified
Temperature- and magnetic-field-dependent resistivity of MgB2 sintered at high temperature and high pressure condition
similarity 0.90C. U. Jung et al. · 2001 · arXiv:cond-mat/0102215
Source status unknown — claims are unverified
The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks
similarity 0.89Y. F. Wu et al. · 2006 · arXiv:cond-mat/0603536
Source status unknown — claims are unverified
Specific heat of MgB_2 after irradiation
similarity 0.89Yuxing Wang et al. · 2002 · arXiv:cond-mat/0208169
Source status unknown — claims are unverified
Low Temperature Fabrication of MgB2
similarity 0.89N. Rogado et al. · 2001 · arXiv:cond-mat/0107534
Source status unknown — claims are unverified