Temperature- and magnetic-field-dependent resistivity of MgB2 sintered at high temperature and high pressure condition
C. U. Jung, Min-Seok Park, W. N. Kang, Mun-Seog Kim, S. Y. Lee, Sung-Ik Lee
arXiv:cond-mat/0102215 · DOI 10.1016/S0921-4534(01)00399-9 · 2001-02-12 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report the temperature- and magnetic-field-dependent resistivity of MgB2 sintered at high temperature and high pressure condition. The superconducting transition width for the resistivity measurement was about 0.4 K, and the low-field magnetization showed a sharp superconducting transition with a transition width of about 1 K. The resistivity in the normal state roughly followed T^2 behavior with smaller residual resistivity ratio (RRR) of 3 over broad temperature region above 100 K rather than reported T^3 behavior with larger RRR value of ~ 20 in the samples made at lower pressures. Also, the resistivity did not change appreciably with the applied magnetic field, which was different from previous report. These differences were discussed with the microscopic and structural change due to the high-pressure sintering.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 37.5 | Pressure unresolved | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 37.5 | Pressure unresolved | onset |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 38 | Pressure unresolved | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 40 | Pressure not reported | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| Sr0.9La0.1CuO2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Thermodynamic and Transport Properties of Superconducting
similarity 0.92D. K. Finnemore et al. · 2001 · arXiv:cond-mat/0102114
Source status unknown — claims are unverified
Fluctuation Magnetoconductance in MgB2
similarity 0.92W. N. Kang et al. · 2001 · arXiv:cond-mat/0103161
Source status unknown — claims are unverified
Effects of pressure on the superconducting properties of magnesium diboride
similarity 0.90X. J. Chen et al. · 2002 · arXiv:cond-mat/0203195
Source status unknown — claims are unverified
Correlation between the residual resistance ratio and magnetoresistance in MgB2
similarity 0.90X. H. Chen et al. · 2001 · arXiv:cond-mat/0107154
Source status unknown — claims are unverified
Effect of sintering temperature under high pressure in the uperconductivity for MgB2
similarity 0.90C. U. Jung et al. · 2001 · arXiv:cond-mat/0102383
Source status unknown — claims are unverified
Hole carrier in MgB_{2} characterized by Hall Measurements
similarity 0.90W. N. Kang et al. · 2001 · arXiv:cond-mat/0102313
Source status unknown — claims are unverified