Growth, structure analysis and anisotropic superconducting properties of MgB2 single crystals

S. Lee; H. Mori; T. Masui; Yu. Eltsev; A. Yamamoto; S. Tajima

doi:10.1143/JPSJ.70.2255

← Back to search

Growth, structure analysis and anisotropic superconducting properties of MgB2 single crystals

S. Lee, H. Mori, T. Masui, Yu. Eltsev, A. Yamamoto, S. Tajima

arXiv:cond-mat/0105545 · DOI 10.1143/JPSJ.70.2255 · 2001-05-29 · Journal of the Physical Society of Japan

T1experimental145 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Here we report the growth of sub-millimeter MgB2 single crystals of various shapes under high pressure in Mg-B-N system. Structure refinement using a single-crystal X-ray diffraction analysis gives lattice parameters a=3.0851(5) A and c=3.5201(5) A with small reliability factors (Rw =0.025, R=0.018), which enables us to analyze the Fourier and Fourier difference maps. The maps clearly show the B sp2 orbitals and covalency of the B-B bonds. The sharp superconducting transitions at Tc =38.1-38.3K were obtained in both magnetization (DTc =0.6K) and resistivity (DTc <0.3K) measurements. Resistivity measurements with magnetic fields applied parallel and perpendicular to the Mg and B sheets reveal the anisotropic nature of this compound, with upper critical field anisotropy ratio of about 2.7.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38.2	Pressure not reported	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38.2	Pressure not reported	unknown