Self Injection length in La0.7 Ca0.3 Mno3-YBa 2Cu3O7-d ferromagnet- superconductor multi layer thin films
S. P. Pai, S. Wanchoo, S. C. Purandare, T. Banerjee, P. R. Apte, A. M. Narsale, R. Pinto
arXiv:cond-mat/0109388 · DOI 10.1007/s12043-002-0231-0 · 2001-09-21 · Pramana
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We have carried out extensive studies on the self-injection problem in barrierless heterojunctions between La0.7Ca0.3MnO3 (LCMO) and YBa2Cu3O7-d (YBCO). The heterojunctions were grown in situ by sequentially growing LCMO and YBCO films on <100> LaAlO3 (LAO) substrate using a pulsed laser deposition (PLD) system. YBCO micro-bridges with 64 microns width were patterned both on the LAO (control) and LCMO side of the substrate. Critical current, Ic, was measured at 77K on both the control side as well as the LCMO side for different YBCO film thickness. It was observed that while the control side showed a Jc of ~2 x 10E6 A/ cm2 the LCMO side showed about half the value for the same thickness (1800 A). The difference in Jc indicates that a certain thickness of YBCO has become 'effectively' normal due to self-injection. From the measurement of Jc at two different thickness' (1800 A and 1500 A) of YBCO both on the LAO as well as the LCMO side, the value of self-injection length (at 77K) was estimated to be ~900 A self-injection length has been quantified. A control experiment carried out with LaNiO3 deposited by PLD on YBCO did not show any evidence of self-injection.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 77 | Pressure not reported | zero_resistance |
Similar papers
3D-XY critical fluctuations of the thermal expansivity in detwinned YBa2Cu3O7-d single crystals near optimal doping
similarity 0.92Volker Pasler et al. · 1998 · arXiv:cond-mat/9804030
Source status unknown — claims are unverified
Measuring the interaction force between a high temperature superconductor and a permanent magnet
similarity 0.92S. O. Valenzuela et al. · 1999 · arXiv:cond-mat/9905084
Source status unknown — claims are unverified
Negative in-plane and out-of-plane magnetoresistivities in optimally doped Bi2Sr2Ca0.8Y0.2Cu2O8+d single crystal
similarity 0.91D. Thopart et al. · 2000 · arXiv:cond-mat/0003149
Source status unknown — claims are unverified
Upper critical fields of MgB2 thin films
similarity 0.90V. Ferrando et al. · 2003 · arXiv:cond-mat/0304478
Source status unknown — claims are unverified
Neutron Irradiation of MgB2 Bulk Superconductors
similarity 0.90M. Eisterer et al. · 2001 · arXiv:cond-mat/0112121
Source status unknown — claims are unverified
Structural and electrical properties of c-axis oriented Y1-xCaxBa2(Cu1-yZny)3O7-delta thin films grown by pulsed laser deposition
similarity 0.89S. H. Naqib et al. · 2003 · arXiv:cond-mat/0312592
Source status unknown — claims are unverified