Structural and electrical properties of c-axis oriented Y1-xCaxBa2(Cu1-yZny)3O7-delta thin films grown by pulsed laser deposition

S. H. Naqib; R. A. Chakalov; J. R. Cooper

doi:10.1016/j.physc.2004.03.249

Structural and electrical properties of c-axis oriented Y1-xCaxBa2(Cu1-yZny)3O7-delta thin films grown by pulsed laser deposition

S. H. Naqib, R. A. Chakalov, J. R. Cooper

arXiv:cond-mat/0312592 · DOI 10.1016/j.physc.2004.03.249 · 2003-12-22 · Physica C-superconductivity and Its Applications

T1experimental20 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Ca- and Zn-subsituted Y1-xCaxBa2(Cu1-yZny)O7-delta (x = 0, 0.05 and y = 0, 0.02, 0.04, 0.05) thin films were grown on SrTiO3 (100) substrates using the pulsed laser deposition (PLD) technique. Effects of various growth parameters on the quality of the film were studied via X-ray diffraction (XRD), atomic force microscopy (AFM), and in-plane resistivity, rhoab(T), measurements. The deposition temperature and oxygen partial pressure were gradually increased to 820C and 1.20 mbar respectively. Films grown under these conditions exhibited good c-axis orientation (primarily limited by the grain size) and low values of the extrapolated residual resistivity, rho(0), at zero temperature. The planar hole content, p, was determined from the room temperature thermopower, S[290K], measurements and the effects of oxygen annealing were also studied. Fully oxygenated samples were found to be overdoped with p ~ 0.195. The Superconducting transition temperature Tc(p), and rho(T,p) showed the expected systematic variations with changing Zn content.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
YBa2(Cu0.98Zn0.02)3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
YBa2(Cu0.96Zn0.04)3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
YBa2(Cu0.95Zn0.05)3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Y0.95Ca0.05Ba2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Y0.95Ca0.05Ba2(Cu0.98Zn0.02)3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Y0.95Ca0.05Ba2(Cu0.96Zn0.04)3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Y0.95Ca0.05Ba2(Cu0.95Zn0.05)3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown