Enhancement of Flux Pinning in Neutron Irradiated MgB$_{2}$ Superconductor
E. Babic, Dj. Miljanic, K. Zadro, I. Kusevic, Z. Marohnic, Dj. Drobac, X. L. Wang, S. X. Dou
arXiv:cond-mat/0112170 · 2001-12-10 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
m-H loops for virgin and neutron irradiated bulk and powder samples of MgB_{2} were measured in the temperature range 5-30 K in magnetic field B<= 1 T. The irradiation at thermal neutron fluences 9*10^{13} and 4.5*10^{14} cm^{-2} caused very small enhancement of m-H loops at lower temperatures (T<20 K), whereas the effect at high temperatures was unclear due to difficulty in achieving exactly the same measurement temperature prior and after irradiation. However, the irradiation at 4.5*10^{15} cm^{-2} produced clear enhancement of m-H loops (hence J_{c}) at all investigated temperatures, which provides the evidence for the enhancement of flux pinning in MgB_{2} due to ion tracks resulting from n+^{10}B reaction. The potential of this technique for the enhancement of flux pinning in high temperature superconductors is briefly discussed.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39 | Pressure not reported | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 38.2 | Pressure not reported | onset |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 38.2 | Pressure not reported | onset |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 37.9 | Pressure not reported | midpoint |
Similar papers
Superconducting properties of MgB probed by radiation-induced disordering
similarity 0.91A. E. Karkin et al. · 2001 · arXiv:cond-mat/0103344
Source status unknown — claims are unverified
Substitution induced pinning in MgB_2 superconductor doped with SiC nano-particles
similarity 0.89S. X. Dou et al. · 2002 · arXiv:cond-mat/0206444
Source status unknown — claims are unverified
Significant improvement of flux pinning and irreversibility field in nano-Carbon doped MgB2 superconductor
similarity 0.89Monika Mudgel et al. · 2008 · arXiv:0803.0373
Source status unknown — claims are unverified
Improved superconducting properties in nanocrystalline bulk MgB_2
similarity 0.89A. Gümbel et al. · 2001 · arXiv:cond-mat/0111585
Source status unknown — claims are unverified
Effects of proton irradiation and ageing on the superconducting properties of single crystalline and polycrystalline MgB2
similarity 0.88G. K. Perkins et al. · 2003 · arXiv:cond-mat/0305255
Source status unknown — claims are unverified
Superconducting fluctuating diamagnetism in neutron irradiated MgB2 in relation to precursor diamagnetism in Al-doped MgB2
similarity 0.88E. Bernardi et al.
Source status unknown — claims are unverified