Crystal growth of MgB2 from Mg-Cu-B melt flux and superconducting properties
D. Souptel, G. Behr, W. Loser, W. Kopylov, M. Zinkevich
arXiv:cond-mat/0208300 · DOI 10.1016/S0925-8388(02)00915-5 · 2002-08-15 · Journal of Alloys and Compounds
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A new method for preparation of single crystals of the superconducting intermetallic MgB2 compound from a Mg-Cu-B melt flux is presented. The high vapour pressure of Mg at elevated temperature is a serious challenge of the preparation process. The approximate thermodynamic calculations of the ternary Mg-Cu-B phase diagram show a beneficial effect of Cu, which extends the range of formation of MgB2 to lower temperatures. Within the as-solidified Mg-Cu-B melt flux the MgB2 compound forms plate-like single crystals up to a size of 0.2 x 0.2 x 0.05 mm3 or alternatively rims peritectically grown around MgB4 particles. AC-susceptibility measurements were conducted with specimen selected from different parts of the as-solidified flux containing MgB2 particles. Peritectically formed MgB2-particles display the highest transition temperature of Tc = 39.2 K and a relatively narrow transition width of DTc = 1.3 K. Other sections of the sample exhibit various superconducting transitions from Tc = 39 K to 7.2 K. This variation of Tc is attributed to a finite homogeneity range of the MgB2 compound whereas significant Cu solid solubility in MgB2 can be excluded.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39.2 | Pressure not reported | unknown |
Similar papers
Low Temperature Fabrication of MgB2
similarity 0.90N. Rogado et al. · 2001 · arXiv:cond-mat/0107534
Source status unknown — claims are unverified
Single crystal growth of MgB2 and thermodynamics of Mg-B-N system at high pressure
similarity 0.90J. Karpinski et al. · 2003 · arXiv:cond-mat/0301051
Source status unknown — claims are unverified
High-pressure high-temperature solution growth, structural, and superconducting properties of Fe-substituted MgB2 single crystals
similarity 0.90N. D. Zhigadlo & R. Puzniak · 2025 · arXiv:2505.16432
Source status unknown — claims are unverified
MgB2 superconductor thin films on Si and Al2O3 substrates
similarity 0.89A. Plecenik et al. · 2001 · arXiv:cond-mat/0105612
Source status unknown — claims are unverified
Anisotropic Superconducting Properties of MgB2 Single Crystals
similarity 0.89Yu. Eltsev et al. · 2002 · arXiv:cond-mat/0202133
Source status unknown — claims are unverified
MgB2 and Mg1-xAlxB2 single crystals: high-pressure growth and physical properties
similarity 0.89J. Karpinski et al. · 2003 · arXiv:cond-mat/0304658
Source status unknown — claims are unverified