Oxygen Content and Valence of Ru in RuSr2(Gd0.75Ce0.25)2Cu2O10(Ru-1222) Magnetosuperconductor
V. P. S. Awana, M. Karppinen, H. Yamauchi, M. Matvejeff, R. S. Liu, L. -Y. Jang
arXiv:cond-mat/0209375 · DOI 10.1023/A:1023490202435 · 2002-09-17 · Journal of Low Temperature Physics
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The valence of Ru was analyzed for two RuSr2(Gd0.75Ce0.25)2Cu2O10 samples with different oxygen contents by Ru LIII edge x ray absorption near-edge structure (XANES) spectroscopy. For the sample as-synthesized in 1 atm O2 the DC magnetization data measured in an applied field of 5 Oe showed a clear branching of the zero-field-cooled (ZFC) and field-cooled (FC) curves at around 100 K, a cusp at 85 K and a diamagnetic transition around 30 K in the ZFC part. A further confirmation for the superconductivity at 30 K was obtained from a resistance vs. temperature measurement. Annealing the as-synthesized sample in 100-atm O2 atmosphere at 420 oC increased the diamagnetic transition temperature from 30 K to 43 K. According to a thermogravimetric analysis, the oxygen content increased accordingly by ca. 0.15 oxygen atoms per formula unit. Quantitative analysis of the XANES spectra using Sr2RuO4 (RuIV) and Sr2GdRuO6 (RuV) as reference materials revealed a valence value of +4.74 and +4.81 for Ru in the as-synthesized and the 100-atm O2-annealed sample, respectively. The obtained result suggests that the valence of Ru in Ru-1222 is affected by the change in oxygen content.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| RuSr2(Gd0.75Ce0.25)2Cu2O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 30 | Pressure unresolved | unknown |
| RuSr2(Gd0.75Ce0.25)2Cu2O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 30 | Pressure unresolved | unknown |
| RuSr2(Gd0.75Ce0.25)2Cu2O10 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 43 | Pressure unresolved | unknown |
Similar papers
Oxygen non-stoichiometry in Ru-1212 and Ru-1222 magnetosuperconductors
similarity 0.94M. Matvejeff et al. · 2002 · arXiv:cond-mat/0211100
Source status unknown — claims are unverified
Magnetic and superconducting properties of RuSr2 Gd1.5Ce0.5Cu2O10-x samples: dependence on the oxygen content and ageing effects
similarity 0.90C. A. Cardoso et al. · 2005 · arXiv:cond-mat/0502674
Source status unknown — claims are unverified
Magnetic Properties of RuSr2RECu2O8 (RE=Gd, Eu) and Ru1-xSr2GdCu2+xO8-y Superconductors
similarity 0.90P. W. Klamut et al. · 2001 · arXiv:cond-mat/0104248
Source status unknown — claims are unverified
Formation and mobility of oxygen vacancies in RuSr2GdCu2O8
similarity 0.89F. Cordero et al. · 2003 · arXiv:cond-mat/0301302
Source status unknown — claims are unverified
Magnetization anomalies in the superconducting state of RuSr2GdCu2O8 and the magnetic study of Sr2GdRuO6
similarity 0.89Thomas P. Papageorgiou et al. · 2002 · arXiv:cond-mat/0205462
Source status unknown — claims are unverified