Superconductivity in CoSr2(Y1-xCax)Cu2O7+d
Y. Morita, H. Yamauchi, M. Karppinen
arXiv:cond-mat/0305198 · DOI 10.1016/S0038-1098(03)00486-1 · 2003-05-09 · Solid State Communications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The roles of aliovalent Ca(II)-for-Y(III) substitution and high-pressure-oxygen annealing in the process of "superconducterizing" the Co-based layered copper oxide, CoSr2(Y1-xCax)Cu2O7+d (Co-1212), were investigated. The as-air-synthesized samples up to x = 0.4 were found essentially oxygen stoichiometric (-0.03 <= d <= 0.00). These samples, however, were not superconductive, suggesting that the holes created by the divalent-for-trivalent cation substitution are trapped on Co in the charge reservoir. Ultra-high-pressure heat treatment carried out at 5 GPa and 500C for 30 min in the presence of Ag2O2 as an excess oxygen source induced bulk superconductivity in these samples. The highest Tc was obtained for the high-oxygen-pressure treated x = 0.3 sample at ~40 K.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| CoSr2(Y0.7Ca0.3)Cu2O7+d Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 40 | Pressure not reported | unknown |
Similar papers
Preparation and properties of superconducting Y(Ba1−xSrx)2Cu4O8
similarity 0.90Takahiro Wada et al.
Source status unknown — claims are unverified
Magnetic and Transport Properties in (=00.4)
similarity 0.89X. G. Luo et al. · 2004 · arXiv:cond-mat/0408081
Source status unknown — claims are unverified
Effect of Sr substitution on the stability of CuO chains in oxygen and nitrogen annealed YBa2-xSrxCu3O(x = 0.0, 0.50, 1.0) superconducting system
similarity 0.89M. A. Ansari et al. · 2003 · arXiv:cond-mat/0311564
Source status unknown — claims are unverified
Induction of superconductivity in Y0.4Pr0.6Ba2-xSrxCu3O7 system with increasing Sr substitution
similarity 0.88V. P. S. Awana et al. · 2004 · arXiv:cond-mat/0408345
Source status unknown — claims are unverified
Role of Ca in enhancing the superconductivity of YBa2Cu3O7−y
similarity 0.88V. P. S. Awana et al.
Source status unknown — claims are unverified
Chemical control of high-Tc superconductivity of the triple-fluorite-layer copper oxide (Cu,Mo)Sr2(Ce,R)3Cu2O11+δ(R=Y,La–Yb)
similarity 0.88M. Karppinen et al.
Source status unknown — claims are unverified