Systematic effects of carbon doping on the superconducting properties of Mg(B$_{1-x}$C$_x$)$_2$

R. H. T. Wilke; S. L. Bud'ko; P. C. Canfield; D. K. Finnemore; Raymond J. Suplinskas; S. T. Hannahs

doi:10.1103/PhysRevLett.92.217003

← Back to search

Systematic effects of carbon doping on the superconducting properties of Mg(B$_{1-x}$C$_x$)$_2$

R. H. T. Wilke, S. L. Bud'ko, P. C. Canfield, D. K. Finnemore, Raymond J. Suplinskas, S. T. Hannahs

arXiv:cond-mat/0312235 · DOI 10.1103/PhysRevLett.92.217003 · 2003-12-10 · Physical review letters

T1experimental332 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The upper critical field, $H_{c2}$, of Mg(B$_{1-x}$C$_x$)$_2$ has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped boron filaments are prepared by CVD techniques, and then these fibers are then exposed to Mg vapor to form the superconducting compound. The transition temperatures are depressed about $1 K/%$ C and $H_{c2}(T=0)$ rises at about $5 T/%$ C. This means that 3.5% C will depress $T_c$ from $39.2 K$ to $36.2 K$ and raise $H_{c2}(T=0)$ from $16.0 T$ to $32.5 T$. Higher fields are probably attainable in the region of 5% C to 7% C. These rises in $H_{c2}$ are accompanied by a rise in resistivity at $40 K$ from about $0.5 μΩcm$ to about $10 μΩcm$. Given that the samples are polycrystalline wire segments, the experimentally determined $H_{c2}(T)$ curves represent the upper $H_{c2}(T)$ manifold associated with $H\perp c$.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	39.2	Pressure not reported	onset
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	39.2	Pressure not reported	onset
Mg(B0.965C0.035)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.2	Pressure not reported	onset
Mg(B0.965C0.035)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.2	Pressure not reported	onset
Mg(B0.983C0.017)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	37.9	Pressure not reported	onset
Mg(B0.983C0.017)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	37.9	Pressure not reported	onset
Mg(B0.9905C0.0095)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38.6	Pressure not reported	onset
Mg(B0.9905C0.0095)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38.6	Pressure not reported	onset
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	40	Pressure not reported	unknown
Mg(B1-xCx)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Mg(B1-xCx)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Mg(B0.90C0.10)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	22	Pressure not reported	unknown
Mg(B0.90C0.10)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Nb3Sn Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown