Upper Critical Fields up to 60T in Dirty Magnesium Diboride Thin Films
C. Ferdeghini, V. Ferrando, C. Tarantini, E. Bellingeri, G. Grasso, A. Malagoli, D. Marre', M. Putti, P. Manfrinetti, A. Pogrebnyakov, J. M. Redwing, X. X. Xi, R. Felici, E. Haanappel
arXiv:cond-mat/0411404 · DOI 10.1109/TASC.2005.848827 · 2004-11-16 · IEEE Transactions on Applied Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Upper critical fields of several magnesium diboride thin films were measured up to 28 T at the Grenoble High Magnetic Field Laboratory (GHMFL) in Grenoble and up to 60 T at the Laboratoire National des Champs Magnetiques Pulses (LNCMP) in Toulouse. The samples were prepared both by pulsed laser deposition (PLD) and hybrid physical chemical vapour deposition (HPCVD) technique; they have critical temperatures between 29 and 39 K and normal state resistivities between 5 and 250 μohmcm; one of them has been intentionally doped with carbon. The measured critical fields were exceptionally high; we obtained the record value of 52 T at 4.2 K in the parallel orientation. In contrast with the BCS predictions, no saturation in Hc2 at low temperature was observed. Furthermore, films with a wide range of resistivity values showed similar critical fields, suggesting that in a two band system resistivity and Hc2 are not trivially linked. The high Hc2 values seem to be related with the expanded c-axis. The structure of one of the samples was carefully investigated with X-ray diffraction at European Synchrotron Radiation Facility (ESRF) in Grenoble.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39 | Pressure not reported | unknown |
Similar papers
Critical flux pinning and enhanced upper critical field in magnesium diboride films
similarity 0.90Milind N. Kunchur et al.
Source status unknown — claims are unverified
High-field superconductivity in alloyed MgB2 thin films
similarity 0.90V. Braccini et al. · 2004 · arXiv:cond-mat/0402001
Source status unknown — claims are unverified
Epitaxial MgB2 thin films on ZrB2 buffer layers: structural characterization by synchrotron radiation
similarity 0.89V. Ferrando et al. · 2004 · arXiv:cond-mat/0406539
Source status unknown — claims are unverified
Thin Film Magnesium Boride Superconductor with Very High Critical Current Density and Enhanced Irreversibility Field
similarity 0.89C. B. Eom et al. · 2001 · arXiv:cond-mat/0103425
Source status unknown — claims are unverified
Very high upper critical fields in MgB2 produced by selective tuning of impurity scattering
similarity 0.88A. Gurevich et al. · 2003 · arXiv:cond-mat/0305474
Source status unknown — claims are unverified
Thick MgB2 film with (101) oriented micro-crystals
similarity 0.88Chinping Chen et al. · 2004 · arXiv:cond-mat/0406325
Source status unknown — claims are unverified