Thick MgB2 film with (101) oriented micro-crystals
Chinping Chen, Xinfeng Wang, Ying Lu, Zhang Jia, Jing-pu Guo, Xiao-nan Wang, Meng Zhu, Xiangyu Xu, Jun Xu, Qing-rong Feng
arXiv:cond-mat/0406325 · DOI 10.1016/j.physc.2004.09.009 · 2004-06-14 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Very thick, ~ 40 $μ$m, clean, and highly textured MgB2 film was effectively grown on an Al2O3 substrate. The fabrication technique is by the hybrid physical-chemical vapor deposition (HPCVD) using B2H6 gas and Mg ingot as the sources. The X-ray diffraction (XRD) analysis shows a highly (101)-oriented MgB2 crystal structure without any impurity detected. There is no signal from the substrate in the XRD spectrum, indicating that the film thickness exceeds the X-ray penetration length. Scanning electron microscopy (SEM) reveals that the film is composed of highly-packed MgB2 micro-crystals with a uniform size distribution of about 2 $μ$m in diameter and 0.2 $μ$m in thickness. According to the compositional analysis of energy-dispersive X-ray spectroscopy (EDX), no oxygen, hence no MgO, exists in the textured film, consistent with the XRD result. Also, the transport properties are similar to those of a single crystal, indicating a clean film of good crystallite. The zero field transition temperatures are determined as TC(onset) = 39.2 K and TC(zero) = 38.4 K, giving a sharp transition typical of a clean sample. The residual resistivity ratio (RRR) is determined as 6.4 and the magnetoreisitance (MR) is about 28 % at 40 K under the applied field of 9 T, which are similar to those of a single crystal. The zero temperature upper critical field, HC2(0), is extrapolated as 19 T from the TC(onset) at applied field up to 9 T.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39.2 | Pressure unresolved | onset |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 38.4 | Pressure unresolved | zero_resistance |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
Similar papers
MgB2 thick film grown on Stainless steel substrate with ductility
similarity 0.91Qing-rong Feng et al. · 2004 · arXiv:cond-mat/0408597
Source status unknown — claims are unverified
Thickness dependence of the properties of epitaxial MgB2 thin films grown by hybrid physical-chemical vapor deposition
similarity 0.91A. V. Pogrebnyakov et al. · 2003 · arXiv:cond-mat/0304164
Source status unknown — claims are unverified
Epitaxial MgB2 superconducting thin films with a transition temperature of 39 Kelvin
similarity 0.90W. N. Kang et al. · 2001 · arXiv:cond-mat/0103179
Source status unknown — claims are unverified
Synthesis of as-grown superconducting MgB_2 thin films by molecular beam epitaxy in UHV conditions
similarity 0.90Y. Harada et al. · 2004 · arXiv:cond-mat/0404252
Source status unknown — claims are unverified
Growth of Epitaxial MgB2 Thick Films with Columnar Structures by Using HPCVD
similarity 0.89Won Kyung Seong et al. · 2007 · arXiv:0709.1884
Source status unknown — claims are unverified
Epitaxial MgB2 thin films on ZrB2 buffer layers: structural characterization by synchrotron radiation
similarity 0.88V. Ferrando et al. · 2004 · arXiv:cond-mat/0406539
Source status unknown — claims are unverified