MgB2 thick film grown on Stainless steel substrate with ductility
Qing-rong Feng, Chinping Chen, Ying Lu, Zhang Zia, Jing-pu Guo, Xiao-nan Wang, Meng Zhu, Jun Xu, Yong-zhong Wang
arXiv:cond-mat/0408597 · DOI 10.1117/12.607297 · 2004-08-27
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning electron microscope (SEM) images reveal that it is consisting of highly dense MgB2 crystals with the size ranging from 0.2 to 3 microns. The superconducting transition occurs at 38 K (Tc, onset) and ends at 27 K (Tc, zero), giving the transition width of 11 K. The fabricated film exhibits high ductility and remains attached to the substrate after it was bent to a curvature of about 200 microns.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 38 | Pressure not reported | onset |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 27 | Pressure not reported | zero_resistance |
Similar papers
Superconducting properties of MgB2 thin films prepared on flexible plastic substrates
similarity 0.91P. Kus et al. · 2002 · arXiv:cond-mat/0206442
Source status unknown — claims are unverified
Thick MgB2 film with (101) oriented micro-crystals
similarity 0.91Chinping Chen et al. · 2004 · arXiv:cond-mat/0406325
Source status unknown — claims are unverified
Properties of MgB2 Films Grown at Various Temperatures by Hybrid Physical-Chemical Vapour Deposition
similarity 0.91K. Chen et al. · 2011 · arXiv:1112.4044
Source status unknown — claims are unverified
Probe to properties of MgB2 thick film on silicon carbide substrate
similarity 0.89Fen Li et al. · 2006 · arXiv:cond-mat/0608549
Source status unknown — claims are unverified
Electrical and structural properties of MgB2 films prepared by sequential deposition of B and Mg on the NbN buffered Si(100) substrate
similarity 0.89S. Chromik et al. · 2004 · arXiv:cond-mat/0401569
Source status unknown — claims are unverified
Superconducting magnesium diboride films on Silicon with Tc0 about 24K grown via vacuum annealing from stoichiometric precursors
similarity 0.89H. Y. Zhai et al. · 2001 · arXiv:cond-mat/0103588
Source status unknown — claims are unverified