Effect of La Doping on Microstructure and Critical Current Density of MgB2
Chandra Shekhar, Rajiv Giri, R S Tiwari, D S Rana, S K Malik, O N Srivastava
arXiv:cond-mat/0507083 · DOI 10.1088/0953-2048/18/9/011 · 2005-07-04 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
In the present study, La-doped MgB_2 superconductors with different doping level (Mg1-xLaxB2; x=0.00, 0.01, 0.03 & 0.05) have been synthesized by solid-state reaction route at ambient pressure. Effect of La doping have been investigated in relation to microstructural characteristics and superconducting properties, particularly intragrain critical current density (Jc). The microstructural characteristics of the as synthesized Mg(La)B2 compounds were studied employing transmission electron microscopic (TEM) technique. The TEM investigations reveal inclusion of LaB6 nanoparticles within the MgB2 grains which provide effective flux pinning centres. The evaluation of intragrain Jc through magnetic measurements on the fine powdered version of the as synthesized samples reveal that Jc of the samples change significantly with the doping level. The optimum result on Jc is obtained for Mg0.97La0.03B2 at 5K, the Jc reaches ~1.4x107A/cm2 in self field, ~2.1 x 106A/cm2 at 1T, ~2.5 x 105A/cm2 at 2.5T and ~1.8 x 104 A/cm2 at 4.5T. The highest value of intragrain Jc in Mg0.97La0.03B2 superconductor has been attributed to the inclusion of LaB6 nanoparticles which are capable of providing effective flux pinning centres.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
| Mg0.99La0.01B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
| Mg0.97La0.03B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
| Mg0.95La0.05B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
Similar papers
High critical current density and improved flux pinning in bulk MgB2 synthesized by Ag addition
similarity 0.91Chandra Shekhar et al. · 2007 · arXiv:cond-mat/0701147
Source status unknown — claims are unverified
Enhancement of the critical current density and flux pinning of MgB2 superconductor by nanoparticle SiC doping
similarity 0.88S. X. Dou et al. · 2002 · arXiv:cond-mat/0207223
Source status unknown — claims are unverified
Improved Critical Current Density of MgB2 Carbon Nanotubes (CNTs) Composite
similarity 0.88Chandra Shekhar et al. · 2006 · arXiv:cond-mat/0608700
Source status unknown — claims are unverified
Improved Irreversibility Behaviour and Critical Current Density in MgB2-Diamond Nanocomposites
similarity 0.87Y. Zhao et al. · 2003 · arXiv:cond-mat/0302365
Source status unknown — claims are unverified
Superconductivity, critical current density, and flux pinning in MgB_{2-x}(SiC)_{x/2} superconductor after SiC nanoparticle doping
similarity 0.87S. X. Dou et al. · 2002 · arXiv:cond-mat/0207093
Source status unknown — claims are unverified
Physical Property Characterization of Bulk MgB2 Superconductor
similarity 0.87V. P. S. Awana et al. · 2008 · arXiv:0807.1203
Source status unknown — claims are unverified