High critical current density and improved flux pinning in bulk MgB2 synthesized by Ag addition
Chandra Shekhar, Rajiv Giri, R. S. Tiwari, S. K. Malik, O. N. Srivastava
arXiv:cond-mat/0701147 · DOI 10.1063/1.2655340 · 2007-01-08 · Journal of Applied Physics
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
In the present investigation, we report a systematic study of Ag admixing in MgB2 prepared by solid-state reaction at ambient pressure. All the samples in the present investigation have been subjected to structural/ microstructural characterization employing x-rays diffraction (XRD) and transmission electron microscopic (TEM) techniques. The magnetization measurements were performed by physical property measurement system (PPMS). The TEM investigations reveal the formation of MgAg nanoparticles in Ag admixed samples. These nanoparticles may enhance critical current density due to their size (~5-20 nm) compatible with coherence length of MgB2 (~5-6 nm). In order to study the flux pinning effect of Ag admixing in MgB2, the evaluation of intragrain critical current density (Jc) has been carried out through magnetic measurements on the fine powdered version of the as synthesized samples. The optimum result on intragrain Jc is obtained for 10 at.% Ag admixed sample at 5K. This corresponds to 9.23x10^7 A/cm^2 in self-field,5.82x10^7 A/cm^2 at 1T,4.24 x10^6 A/cm^2 at 3.6T and 1.52x10^5 A/cm^2 at 5T. However, intragrain Jc values for MgB2 sample without Ag admixing are 2.59x10^6 A/cm^2,1.09x10^6A/cm^2,4.53x10^4 A/cm^2 and 2.91x10^3A/cm^2 at 5 K in self field, 1T, 3.6T and 5T respectively.. The high value of intragrain Jc for Ag admixed MgB2 superconductor has been attributed to the inclusion of MgAg nanoparticles into the crystal matrix of MgB2, which are capable of providing effective flux pinning centres. A feasible correlation between microstructural features and superconducting properties has been put forward.
Similar papers
Effect of La Doping on Microstructure and Critical Current Density of MgB2
similarity 0.91Chandra Shekhar et al. · 2005 · arXiv:cond-mat/0507083
Source status unknown — claims are unverified
Supercurrents in Magnesium Diboride/Metal Composite Wire
similarity 0.90M. J. Holcomb · 2005 · arXiv:cond-mat/0506779
Source status unknown — claims are unverified
Improved Critical Current Density of MgB2 Carbon Nanotubes (CNTs) Composite
similarity 0.89Chandra Shekhar et al. · 2006 · arXiv:cond-mat/0608700
Source status unknown — claims are unverified
Enhancement of the critical current density and flux pinning of MgB2 superconductor by nanoparticle SiC doping
similarity 0.89S. X. Dou et al. · 2002 · arXiv:cond-mat/0207223
Source status unknown — claims are unverified
Enhanced critical current density of MgB2 superconductor synthesized in high magnetic fields
similarity 0.89Yanwei Ma et al. · 2006 · arXiv:cond-mat/0601245
Source status unknown — claims are unverified
Improved Irreversibility Behaviour and Critical Current Density in MgB2-Diamond Nanocomposites
similarity 0.88Y. Zhao et al. · 2003 · arXiv:cond-mat/0302365
Source status unknown — claims are unverified