High-pressure synthesis and superconductivity of Ca2-xNaxCuO2Cl2
N. D. Zhigadlo, J. Karpinski
arXiv:cond-mat/0606568 · DOI 10.1016/J.PHYSC.2007.03.292 · 2006-06-22 · Physica C: Superconductivity and its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Ca2-xNaxCuO2Cl2 is a structural analogue to the La2-xSrxCuO4 superconductor. By substituting Na+ for Ca2+ mobile holes are introduced into the CuO2 planes. A series of experiments shows that the Na content x depends not only on the pressure during synthesis but also on the synthesis temperature and time. Ca2-xNaxCuO2Cl2 crystals (x=0.10 and Tc,on=13.5 K) up to 1x1x0.05 mm3 have been grown by a flux method at 35 kbar and the temperature was slowly ramped from 1250 C to 1050 C within 8 h. Applying higher synthesis pressure (up to 55 kbar) and temperature (up to 1700 C) results in polycrystalline samples with highest Tc,on=28.0 K at x=0.20. Further experiments are under way to optimize conditions to grow crystals with extended concentration of Na and Tc characteristic for optomally doped and overdoped regions.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Ca1.9Na0.1CuO2Cl2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 13.5 | Pressure not reported | onset |
| Ca1.8Na0.2CuO2Cl2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 28 | Pressure not reported | onset |
Similar papers
Synthesis and Bulk Properties of Oxychloride Superconductor Ca2-xNaxCuO2Cl2
similarity 0.94N. D. Zhigadlo et al. · 2007 · arXiv:0712.3377
Source status unknown — claims are unverified
Growth and structural characterization of large superconducting crystals of La2−xCa1+xCu2O6
similarity 0.89J. A. Schneeloch et al.
Source status unknown — claims are unverified
Supersolid Phases of a Doped Valence-Bond Quantum Antiferromagnet: Evidence for a Coexisting Superconducting Order Parameter
similarity 0.88Marcin Raczkowski & Didier Poilblanc
Source status unknown — claims are unverified
Bulk charge density wave and electron-phonon coupling in superconducting copper oxychlorides
similarity 0.88Laura Chaix et al. · 2022 · arXiv:2203.15311
Source status unknown — claims are unverified
Superconductivity in CoSr2(Y1-xCax)Cu2O7+d
similarity 0.88Y. Morita et al. · 2003 · arXiv:cond-mat/0305198
Source status unknown — claims are unverified
Structure and superconductivity without apical oxygens in (Ca,Na)2CuO2Cl2
similarity 0.88D. N. Argyriou et al.
Source status unknown — claims are unverified