Low temperature synthesis and pressure induced insulator-metal transition of the newly found NdFeAsO0.75
Qingping Ding, Yangguang Shi, Hongbo Huang, Shaolong Tang, Shaoguang Yang
arXiv:0806.0976 · 2008-06-05 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
As low as 900 oC, iron-based layered quaternary compound NdFeAsO0.75 was synthesized through solid state reaction method. XRD measurements illustrate almost pure phase of tetragonal phase NdFeAsO was formed. The synthesis temperature in our experiment is the lowest among all the reported methods without the help of any mineralizer. After further treatment under high pressure of 6 GPa at temperature of 1300 oC for 2 hours, the electrical transport property of NdFeAsO0.75 was transformed from insulator-like to metal- like behavior.
Similar papers
One-step atmospheric pressure synthesis of the ground state of Fe based LaFeAsO1-d superconductor
similarity 0.88V. P. S. Awana et al. · 2008 · arXiv:0805.0214
Source status unknown — claims are unverified
Physical property characterization of single step synthesized NdFeAsO0.80F0.20 bulk 50K superconductor
similarity 0.87V. P. S. Awana et al. · 2010 · arXiv:1003.0273
Source status unknown — claims are unverified
Low-Temperature Rapid Synthesis and Superconductivity of Fe-Based Oxypnictide Superconductors
similarity 0.87Fang, Ai-Hua et al. · 2010 · arXiv:1004.0988
Source status unknown — claims are unverified
Superconductivity in iron-based F-doped layered quaternary compound Nd[O1-xFx]FeAs
similarity 0.86Zhi-An Ren* et al. · 2008 · arXiv:0803.4234
Source status unknown — claims are unverified
Synthesis and Microstructural Studies of Iron Based LaO1-xFxFeAs Superconducting Materials
similarity 0.86Chandra Shekhar et al. · 2008 · arXiv:0806.1661
Source status unknown — claims are unverified
Pressure-induced superconductivity in PrOxFeAs
similarity 0.85Qingping Ding et al. · 2008 · arXiv:0806.2379
Source status unknown — claims are unverified