Low-Temperature Rapid Synthesis and Superconductivity of Fe-Based Oxypnictide Superconductors
Fang, Ai-Hua, Huang, Fu-Qiang, Xie, Xiao-Ming, Jiang, Mian-Heng
arXiv:1004.0988 · 2010-04-08
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
we were able to develop a novel method to synthesize Fe-based oxypnictide superconductors. By using LnAs and FeO as the starting materials and a ball-milling process prior to solid-state sintering, Tc as high as 50.7 K was obtained with the sample of Sm 0.85Nd0.15FeAsO0.85F0.15 prepared by sintering at temperatures as low as 1173 K for times as short as 20 min.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Sm0.85Nd0.15FeAsO0.85F0.15 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 50.7 | Pressure not reported | unknown |
Similar papers
Low-temperature synthesis of SmO0.8F0.2FeAs superconductor with Tc = 56.1K
similarity 0.92Chunlei Wang et al. · 2010 · arXiv:1003.0171
Source status unknown — claims are unverified
One step synthesis of SmO1-xFxFeAs bulks with Tc = 54.6 K: High upper critical field and critical current density
similarity 0.91Yanwei Ma et al. · 2008 · arXiv:0806.2839
Source status unknown — claims are unverified
Fast synthesis of Fe1.1Se1-xTex superconductors in a self-heating and furnace-free way
similarity 0.89Guang-Hua Liu et al. · 2016 · arXiv:1602.00880
Source status unknown — claims are unverified
Transition Temperature and Upper Critical Field in SmFeAsO1-xFx Synthesized at Low Heating Temperatures
similarity 0.89S. J. Singh et al. · 2013 · arXiv:1303.4163
Source status unknown — claims are unverified
Low-temperature synthesis of SmFeAsO0.7F0.3 wires with high transport critical current density
similarity 0.89Lei Wang et al. · 2010 · arXiv:1003.0153
Source status unknown — claims are unverified
One-step atmospheric pressure synthesis of the ground state of Fe based LaFeAsO1-d superconductor
similarity 0.89V. P. S. Awana et al. · 2008 · arXiv:0805.0214
Source status unknown — claims are unverified