One step synthesis of SmO1-xFxFeAs bulks with Tc = 54.6 K: High upper critical field and critical current density
Yanwei Ma, Zhaoshun Gao, Lei Wang, Yanpeng Qi, Dongliang Wang, Xianping Zhang
arXiv:0806.2839 · 2008-06-17 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A safe, simple and easily scaleable one-step sintering method is proposed to fabricate newly discovered superconductors of SmO1-xFxFeAs. Superconducting transition with the onset temperature of 54.6 K and high critical fields Hc2(0) >=200 T were confirmed in SmO1-xFxFeAs with x = 0.3. At 5 K and self field, critical current density Jc estimated from the magnetization hysteresis using the whole sample size and the average particle size reached 8.5x10^3 and 1.2x10^6 A/cm^2, respectively. Moreover, the Jc exhibited a very weak dependence on magnetic field. Microstructural characterizations revealed that the whole sample Jc improvement could be achieved by either perfect texture or optimization of fabrication process in this strongly-layered superconductor. Our results clearly demonstrated that one-step synthesis technique is unique and versatile and hence can be tailored easily for other rare earth derivatives of REFeAsO superconductors.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SmO0.7F0.3FeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 54.6 | Pressure not reported | onset |
Similar papers
Low-temperature synthesis of SmO0.8F0.2FeAs superconductor with Tc = 56.1K
similarity 0.93Chunlei Wang et al. · 2010 · arXiv:1003.0171
Source status unknown — claims are unverified
Anomalous Transport Properties and Phase Diagram of the FeAs-Based SmFeAsO1−xFx Superconductors
similarity 0.87R. H. Liu et al.
Source status unknown — claims are unverified
Upper critical field, critical current density and activation energy of the new La1-xSmxOF0.5BiS2 (x = 0.2, 0.8) superconductor
similarity 0.86G. Kalai Selvan et al. · 2015 · arXiv:1507.06247
Source status unknown — claims are unverified
Superconductivity in oxygen-annealed FeTe1-xSx single crystal
similarity 0.86Yoshikazu Mizuguchi et al. · 2010 · arXiv:1009.3315
Source status unknown — claims are unverified
Superconductivity induced by U-doping in the SmFeAsO system
similarity 0.86Bo Huang et al. · 2013 · arXiv:1302.5155
Source status unknown — claims are unverified
Flux free growth of superconducting FeSe single crystals
similarity 0.86P. K. Maheshwari et al. · 2016 · arXiv:1606.08201
Source status unknown — claims are unverified