Low-temperature synthesis of SmO0.8F0.2FeAs superconductor with Tc = 56.1K
Chunlei Wang, Zhaoshun Gao, Lei Wang, Yanpeng Qi, Dongliang Wang, Chao Yao, Zhiyu Zhang, Yanwei Ma
arXiv:1003.0171 · DOI 10.1088/0953-2048/23/5/055002 · 2010-02-28 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report a systematic study on the effect of sintering temperature on the structural and superconducting properties of nominal SmO0.8F0.2FeAs fabricated by simple one-step solid state reaction method. A detailed correlation between the sintering temperature, structure, onset transition temperature (Tc) and critical current density (Jc) has been found in all samples of each batch. Most importantly, samples sintered at a low temperature clearly shows high Tc, for example the Tc of the samples sintered at 850C is even above 53 K, and the samples prepared at 1000C display the highest Tc of 56.1 K reported so far. Furthermore, the samples sintered at 1000C also show the highest RRR and the lowest resistivity(57K), indicating the low impurity scattering and enhanced carrier density. However, the maximum Jc of 10510 A/cm^2 at 5 K in self field was achieved in the samples sintered at 1100oC. The dependence of Tc on a-axis lattice constant indicates that the sintering temperature has strong influence on the effective substitution level of F for O. This result suggests that annealing at a temperature of ~1000C seems much better for obtaining high quality 1111 phase oxypnictides, compared to commonly used temperatures of around 1200C.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SmO0.8F0.2FeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 56.1 | Pressure not reported | onset |
Similar papers
One step synthesis of SmO1-xFxFeAs bulks with Tc = 54.6 K: High upper critical field and critical current density
similarity 0.93Yanwei Ma et al. · 2008 · arXiv:0806.2839
Source status unknown — claims are unverified
Transition Temperature and Upper Critical Field in SmFeAsO1-xFx Synthesized at Low Heating Temperatures
similarity 0.92S. J. Singh et al. · 2013 · arXiv:1303.4163
Source status unknown — claims are unverified
Effect of spark plasma sintering on the superconducting properties of Sm-based oxypnictide
similarity 0.91Mohammad Azam et al. · 2025 · arXiv:2505.16657
Source status unknown — claims are unverified
α-FeAs-free SmFeAsO1-xFx by low temperature sintering with slow cooling
similarity 0.90Masaya Fujioka et al. · 2013 · arXiv:1303.1309
Source status unknown — claims are unverified
Superconductivity at 56 K in Samarium-doped SrFeAsF
similarity 0.90G. Wu et al. · 2008 · arXiv:0811.0761
Source status unknown — claims are unverified
Enhancement in superconducting transition temperature and upper critical field of LaO0.8F0.2FeAs with antimony doping
similarity 0.89S. J. Singh et al. · 2008 · arXiv:0810.2362
Source status unknown — claims are unverified