Transition Temperature and Upper Critical Field in SmFeAsO1-xFx Synthesized at Low Heating Temperatures
S. J. Singh, J. Shimoyama, A. Yamamoto, H. Ogino, K. Kishio
arXiv:1303.4163 · DOI 10.1109/TASC.2013.2239352 · 2013-03-18 · IEEE Transactions on Applied Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Low-temperature synthesis is a promising and potentially effective method for improving superconducting properties. We report on the fabrication of polycrystalline samples of SmFeAsO1-xFx with nominal x content varying in a wide range of x = 0-0.35 synthesized at 900 deg C. This synthesis temperature is around 300 deg C lower than the conventional synthesis temperature. The variation in the lattice parameters and transition temperature (Tc) of various F-doped samples indicates that reduction of the unit cell volume (V) seems to be the main reason for the rise of Tc up to 57.8 K. Magnetoresistance measurements showed that the upper critical field slope (dHc2/dT) increased with increasing F concentration up to x = 0.2, where it reached a maximum value of -8 T/K corresponding to a coherence length of 10 angstrom. At still higher F doping levels, dHc2/dT and the low field Jc decreased; above 0.5 T, however, Jc had almost the same value. Compared with previous reports, the present synthesis route with low synthesis temperatures and commonly available FeF2 as the source of F is more effective at introducing F into the SmFeAsO system and thereby resulting in improved superconducting properties for the system. In addition, this new sample preparation method also reduces unnecessary problems such as the evaporation of F and reaction between the crucible and superconductor during the solid-state reaction.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SmFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 57.8 | Pressure not reported | unknown |
Similar papers
One step synthesis of SmO1-xFxFeAs bulks with Tc = 54.6 K: High upper critical field and critical current density
similarity 0.92Yanwei Ma et al. · 2008 · arXiv:0806.2839
Source status unknown — claims are unverified
Thermally activated energy and critical magnetic fields of SmFeAsOF
similarity 0.91Y. Z. Zhang et al. · 2009 · arXiv:0904.3625
Source status unknown — claims are unverified
Phase Diagram and Quantum Critical Point in Newly Discovered Superconductors: SmO_{1-x}F_xFeAs
similarity 0.91R. H. Liu et al. · 2008 · arXiv:0804.2105
Source status unknown — claims are unverified
Low-temperature synthesis of SmFeAsO0.7F0.3 wires with high transport critical current density
similarity 0.90Lei Wang et al. · 2010 · arXiv:1003.0153
Source status unknown — claims are unverified
Effect of starting materials on the superconducting properties of SmFeAsO1-xFx tapes
similarity 0.89Chunlei Wang et al. · 2012 · arXiv:1201.6522
Source status unknown — claims are unverified
Superconductivity induced by U-doping in the SmFeAsO system
similarity 0.89Bo Huang et al. · 2013 · arXiv:1302.5155
Source status unknown — claims are unverified