Effect of starting materials on the superconducting properties of SmFeAsO1-xFx tapes
Chunlei Wang, Chao Yao, Xianping Zhang, Zhaoshun Gao, Dongliang Wang, Chengduo Wang, He Lin, Yanwei Ma, Satoshi Awaji, Kazuo Watanabe
arXiv:1201.6522 · DOI 10.1088/0953-2048/25/3/035013 · 2012-01-31 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
SmFeAsO1-xFx tapes were prepared using three kinds of starting materials. It shows that the starting materials have an obvious effect on the impurity phases in final superconducting tapes. Compared with the other samples, the samples fabricated by SmAs, FeO, Fe2As, and SmF3 have the smallest arsenide impurity phase and voids. As a result, these samples possess much denser structure and better grain connectivity. Moreover, among the three kinds of samples fabricated in this work, this kind of sample has the highest zero-resistivity temperature ~40 K and largest critical current density ~4600 A/cm^2 in self-field at 4.2 K. This is the highest Jc values reported so far for SmFeAsO1-xFx wires and tapes.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SmFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 40 | Pressure not reported | zero_resistance |
Similar papers
Enhancement of transport critical current density of SmFeAsO1-xFx tapes fabricated by an ex-situ powder-in-tube method with a Sn-presintering process
similarity 0.90Qianjun Zhang et al. · 2014 · arXiv:1405.6835
Source status unknown — claims are unverified
Transition Temperature and Upper Critical Field in SmFeAsO1-xFx Synthesized at Low Heating Temperatures
similarity 0.89S. J. Singh et al. · 2013 · arXiv:1303.4163
Source status unknown — claims are unverified
High critical current density and low anisotropy in textured Sr1-xKxFe2As2 tapes for high field applications
similarity 0.89Zhaoshun Gao et al. · 2013 · arXiv:1302.4583
Source status unknown — claims are unverified
Low-temperature synthesis of SmO0.8F0.2FeAs superconductor with Tc = 56.1K
similarity 0.89Chunlei Wang et al. · 2010 · arXiv:1003.0171
Source status unknown — claims are unverified
Oxypnictide SmFeAs(O,F) superconductor: a candidate for high-field magnet applications
similarity 0.89Kazumasa Iida et al. · 2013 · arXiv:1307.1282
Source status unknown — claims are unverified
Antimony Doping Effect on the Superconducting Properties of SmFeAs(O,F)
similarity 0.88Azam, Mohammad et al. · 2023 · arXiv:2311.13908
Source status unknown — claims are unverified