Synthesis, crystal structure, microstructure, transport and magnetic properties of SmFeAsO and SmFeAs(O0.93F0.07)
A. Martinelli, M. Ferretti, P. Manfrinetti, A. Palenzona, M. Tropeano, M. R. Cimberle, C. Ferdeghini, R. Valle, M. Putti, A. S. Siri
arXiv:0806.2205 · DOI 10.1088/0953-2048/21/9/095017 · 2008-06-13 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
SmFeAsO and the isostructural superconducting SmFeAs(O0.93F0.07) samples were prepared. Characterization by means of Rietveld refinement of X-ray powder diffraction data, scanning electron microscope observation, transmission electron microscope analysis, resistivity and magnetization measurements were carried out. Sintering treatment strongly improves the grain connectivity, but, on the other hand, induces a competition between the thermodynamic stability of the oxy-pnictide and Sm2O3, hence worsening the purity of the sample. In the pristine sample both magnetization and resistivity measurements clearly indicate that two different sources of magnetism are present: the former related to Fe ordering at 140 K and the latter due to the Sm ions that orders antiferromagnetically at low temperature. The feature at 140 K disappears in the F-substituted sample and, at low temperatures a superconducting transition appears. The magnetoresistivity curves of the F-substituted sample probably indicates very high critical field values.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SmFeAs(O0.93F0.07) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| SmFeAs(O0.93F0.07) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Interplay of composition, structure, magnetism, and superconductivity in SmFeAs1−xPxO1−y
similarity 0.92N. D. Zhigadlo et al.
Source status unknown — claims are unverified
Interplay of composition, structure, magnetism, and superconductivity in SmFeAs1-xPxO1-y
similarity 0.92N. D. Zhigadlo et al. · 2011 · arXiv:1107.5715
Source status unknown — claims are unverified
Superconductivity induced by U doping in the SmFeAsO system
similarity 0.90Bo Huang et al.
Source status unknown — claims are unverified
Local structural distortions and their role in superconductivity in SmFeAsOF superconductors
similarity 0.90Kapil Ingle et al. · 2014 · arXiv:1405.3086
Source status unknown — claims are unverified
Th substituted SmFeAsO: structural details and superconductivity with Tc above 50 K
similarity 0.90N. D. Zhigadlo et al. · 2010 · arXiv:1006.0126
Source status unknown — claims are unverified
Oxypnictide SmFeAs(O,F) superconductor: a candidate for high-field magnet applications
similarity 0.89Kazumasa Iida et al. · 2013 · arXiv:1307.1282
Source status unknown — claims are unverified