Superconductivity at 14K in the Co-doped SmFe0.9Co0.1AsO

V. P. S. Awana; Arpita Vajpayee; Anand Pal; Monika Mudgel; R. S. Meena; H. Kishan

← Back to search

Superconductivity at 14K in the Co-doped SmFe0.9Co0.1AsO

V. P. S. Awana, Arpita Vajpayee, Anand Pal, Monika Mudgel, R. S. Meena, H. Kishan

arXiv:0902.3894 · 2009-02-23 · arXiv: Superconductivity

T1theoretical3 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report superconductivity in the SmFe0.9Co0.1AsO system being prepared by most easy and versatile single step solid-state reaction route. The parent compound SmFeAsO is non-superconducting but shows the spin density wave (SDW) like antiferromagnetic ordering at around 140K. To destroy the antiferromagnetic ordering and to induce the superconductivity in the parent system, the Fe2+ is substituted partially by Co3+. Superconductivity appears in SmFe0.9Co0.1AsO system at around 14K. The Co doping suppresses the SDW anomaly in the parent compound and induces the superconductivity. Magnetization measurements show clearly the onset of superconductivity with Tcdia at 14K. The isothermal magnetization measurements exhibit the lower critical fields (Hc1) to be around 200Oe at 2 K. The bulk superconductivity of the studied SmFe0.9Co0.1AsO sample is further established by open diamagnetic M(H) loops at 2, and 5K. Normal state (above Tc) linear isothermal magnetization M(H) plots excluded presence of any ordered magnetic impurity in the studied compound.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
SmFe0.9Co0.1AsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14	Pressure not reported	onset