Appearance and disappearance of superconductivity with Fe site Co substitution in SmFe1-xCoxAsO (x = 0.0 to 1.0)

V. P. S. Awana; Anand Pal; Mushahid Hussain; H. Kishan

doi:10.1007/S10948-010-0910-X

← Back to search

Appearance and disappearance of superconductivity with Fe site Co substitution in SmFe1-xCoxAsO (x = 0.0 to 1.0)

V. P. S. Awana, Anand Pal, Mushahid Hussain, H. Kishan

arXiv:1007.5121 · DOI 10.1007/S10948-010-0910-X · 2010-07-29 · Journal of Superconductivity and Novel Magnetism

T1theoretical7 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report synthesis, structural details and magnetization of SmFe1-xCoxAsO with x ranging from 0.0 to 1.0 at close interval of 0.10. It is found that Co substitutes fully at Fe site in SmFeAsO in an iso-structural lattice with slightly compressed cell. The parent compound exhibited known spin density wave (SDW) character below 150K. Successive doping of Co at Fe site suppressed the SDW transition for x = 0.05 and later induced superconductivity for x = 0.10, 0.15 and 0.20 respectively at 14, 15.5 and 9K. The appearance of bulk superconductivity is established by wide open isothermal magnetization M(H) loops. For higher content of Co i.e. x \geq 0.30, superconductivity is not observed. Clearly the Co substitution at Fe site in SmFe1-xCoxAsO diminishes the Fe SDW character (x=0.05), introduces bulk superconductivity for x from 0.10 to 0.20 and finally becomes a non-superconductor. The SmCoAsO also exhibits a secondary AFM like transition at below around 50 K. The reported AFM ordering of Sm spins is seen from heat capacity Cp(T) at 4.5 K and the same remains invariant with Co doping in SmFe1-xCoxAsO. Further the FM ordering of Co-spins (seen in magnetization measurements) is not evident in Cp(T) studies, suggesting weak correlations between ordered Co-spins in these systems.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
SmFe0.90Co0.10AsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14	Pressure not reported	unknown
SmFe0.85Co0.15AsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15.5	Pressure not reported	unknown
SmFe0.80Co0.20AsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9	Pressure not reported	unknown