Superconductivity in SmFe1-xCoxAsO (x = 0.0 to 0.30)

V. P. S. Awana; Anand Pal; Arpita Vajpayee; Monika Mudgel; H. Kishan; Mushahid Husain; R. Zeng; S. Yu; K. Yamaura; E. Takayama-Muromachi

doi:10.1063/1.3366601

Superconductivity in SmFe1-xCoxAsO (x = 0.0 to 0.30)

V. P. S. Awana, Anand Pal, Arpita Vajpayee, Monika Mudgel, H. Kishan, Mushahid Husain, R. Zeng, S. Yu, K. Yamaura, E. Takayama-Muromachi

arXiv:0912.0999 · DOI 10.1063/1.3366601 · 2009-12-05 · Journal of Applied Physics

T1theoretical14 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report synthesis, structural details and magnetization of SmFe1-xCoxAsO with x ranging from 0.0 to 0.30. It is found that Co substitutes fully at Fe site in SmFeAsO in an iso-structural lattice with slightly compressed cell. The parent compound exhibited known spin density wave (SDW) character below at around 140 K. Successive doping of Co at Fe site suppressed the SDW transition for x = 0.05 and later induced superconductivity for x = 0.10, 0.15 and 0.20 respectively at 14, 15.5 and 9K. The lower critical field as seen from magnetization measurements is below 200Oe. The appearance of bulk superconductivity is established by wide open isothermal magnetization M(H) loops. Superconductivity is not observed for higher content of Co i.e. x = 0.30. Clearly the Co substitution at Fe site in SmFe1-xCoxAsO diminishes the Fe SDW character, introduces bulk superconductivity for x between 0.10 and 0.20 and finally becomes non-superconducting for x above 0.20. The Fe2+ site Co3+ substitution injects mobile electrons to the system and superconductivity appears, however direct substitution introduces simultaneous disorder in superconducting FeAs layer and thus superconductivity disappears for higher content of Co.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
SmFe0.90Co0.10AsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14	Pressure not reported	unknown
SmFe0.85Co0.15AsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15.5	Pressure not reported	unknown
SmFe0.80Co0.20AsO Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9	Pressure not reported	unknown