Effect of higher borides and inhomogeneity of oxygen distribution on critical current density of undoped and doped magnesium diboride
T. A. Prikhna, W. Gawalek, V. M. Tkach, N. I. Danilenko, Ya M. Savchuk, S. N. Dub, V. E. Moshchil, A. V. Kozyrev, N. V. Sergienko, M. Wendt, V. S. Melnikov, J. Dellith, H Weber, M Eisterer, Ch Schmidt, T Habisreuther, D Litzkendorf, J Vajda, A. P. Shapovalov, V. Sokolovsky, P. A. Nagorny, V. B. Sverdun, J. Kosa, F. Karau, A. V. Starostina
arXiv:0912.4889 · DOI 10.1088/1742-6596/234/1/012031 · 2009-12-24 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The effect of doping with Ti, Ta, SiC in complex with synthesis temperature on the amount and distribution of structural inhomogeneities in MgB2 matrix of high-pressuresynthesized-materials (2 GPa) which can influence pining: higher borides (MgB12) and oxygen-enriched Mg-B-O inclusions, was established and a mechanism of doping effect on jc increase different from the generally accepted was proposed. Near theoretically dense SiC-doped material exhibited jc= 1000000 A/sq. cm in 1T field and Hirr =8.5 T at 20 K. The highest jc in fields above 9, 6, and 4 T at 10, 20, and 25 K, respectively, was demonstrated by materials synthesized at 2 GPa, 600 oC from Mg and B without additions (at 20 K jc= 100 A/sq. cm in 10 T field). Materials synthesized from Mg and B taken up to 1:20 ratio were superconductive. The highest jc (60000 A/sq. cm at 20 K in zero field, Hirr= 5 T) and the amount of SC phase (95.3 percents of shielding fraction), Tc being 37 K were demonstrated by materials having near MgB12 composition of the matrix. The materials with MgB12 matrix had a doubled microhardness of that with MgB2 matrix (25 GPa and 13.08 GPa, at a load of 4.9 N, respectively).
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB12 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 37 | 2 GPa | unknown |
Similar papers
Inhomogeneity of Magnesium Diboride Structure and its Effect on Critical Current Density
similarity 0.95T. Prikhna et al. · 2009 · arXiv:0912.4903
Source status unknown — claims are unverified
Higher borides and oxygen-enriched Mg-B-O inclusions as possible pinning centers in nanostructural magnesium diboride and the influence of additives on their formation
similarity 0.91Tatiana Prikhna et al. · 2010 · arXiv:1001.1904
Source status unknown — claims are unverified
Enhancement of the critical current density and flux pinning of MgB2 superconductor by nanoparticle SiC doping
similarity 0.90S. X. Dou et al. · 2002 · arXiv:cond-mat/0207223
Source status unknown — claims are unverified
High-pressure synthesis of MgB2 with addition of Ti
similarity 0.89T. A. Prikhna et al. · 2003 · arXiv:cond-mat/0306013
Source status unknown — claims are unverified
Superconductivity, critical current density, and flux pinning in MgB_{2-x}(SiC)_{x/2} superconductor after SiC nanoparticle doping
similarity 0.89S. X. Dou et al. · 2002 · arXiv:cond-mat/0207093
Source status unknown — claims are unverified
Effect of Mg/B ratio on the superconductivity of MgB2 bulk with SiC addition
similarity 0.89Y. Zhang et al.
Source status unknown — claims are unverified