High-pressure synthesis of MgB2 with addition of Ti
T. A. Prikhna, W. Gawalek, Ya. M. Savchuk, V. E. Moshchil, N. V. Sergienko, R. Hergt, M. Wendt, S. N. Dub, Ch. Schmidt, J. Dellith, V. S. Melnikov, T. Habisreuther, D. Litzkendorf, P. A. Nagorny
arXiv:cond-mat/0306013 · DOI 10.1016/j.physc.2003.10.021 · 2003-06-01 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The MgB2 - based material high-pressure synthesized at 2 GPa and 800 C for 1 h from Mg and B (taken in the stoichiometry ratio of MgB2) with addition of 2-10 wt% of Ti demonstrated the critical current density (jc) higher than 100 kA/cm^2 at 33 K in 0 T field and at 20 K up to 3 T. At 20 K the critical current density higher than 10 kA/cm^2 was observed up to 5 T field. In the magnetic field up to 2 T high-pressure synthesized MgB2 (with 10 % of Ti) at 20 K behaves in the same manner as Nb3Sn at 4.2 K. In XRD patterns of magnesium diboride with the Ti added, we observed no evidence of titanium diboride or unreacted titanium and only one compound with titanium was identified, namely, titanium dihydride TiH2 (or more strictly TiH1.924). The sample with the highest critical current density and irreversible field in the temperature range of 25-10 K contained some amount of pure Mg that was rather homogeneously dispersed in the material. The critical currents and irreversible fields of magnesium diboride synthesized at high pressure with Ti added are higher than those in the case where Ta has been added.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Synthesis and Sintering of MgB2 Under High Pressure
similarity 0.93T. A. Prikhna et al. · 2002 · arXiv:cond-mat/0204068
Source status unknown — claims are unverified
The high-pressure synthesis of MgB2
similarity 0.90T. A. Prikhna et al. · 2001 · arXiv:cond-mat/0109216
Source status unknown — claims are unverified
CVD routes to MgB2 conductors
similarity 0.88D. K. Finnemore et al. · 2003 · arXiv:cond-mat/0302242
Source status unknown — claims are unverified
Effects of high pressure on the physical properties of MgB2
similarity 0.88T. Prikhna et al. · 2010 · arXiv:1005.2092
Source status unknown — claims are unverified
Titanium additions to MgB2 conductors
similarity 0.88N. E. Anderson, et al. · 2003 · arXiv:cond-mat/0302245
Source status unknown — claims are unverified
Superconductivity in high-pressure synthesized pure and doped MgB2 compounds
similarity 0.87P. Toulemonde et al. · 2002 · arXiv:cond-mat/0206409
Source status unknown — claims are unverified