T. A. Prikhna, W. Gawalek, A. B. Surzhenko, N. V. Sergienko, V. E. Moshchil, T. Habisreuther, V. S. Melnikov, S. N. Dub, P. A. Nagorny, M. Wendt, Ya. M. Savchuk, D. Litzkendorf, J. Dellith, S. Kracunovska, Ch. Schmidt
arXiv:cond-mat/0109216 · 2001-09-12 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be manufactured. By a short-term (1h) high-pressure (2GPa) synthesis from Mg and B we have obtained samples 2.4-2.5 g/cm3 in density, 12.1-15.6 GPa in microhardness (under 4.96 N load), 170-200 kA/cm2 at 10 K and 58-62 kA/cm2 at 20 K in critical current density at a magnetic field of 1T. Samples demonstrated 8.5 T irreversible field at 10 K and 5.5 T at 20 K. The Ta positive influence on SC properties of MgB2 has been observed.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | 2 GPa | unknown |
Similar papers
Effects of high pressure on the physical properties of MgB2
similarity 0.91T. Prikhna et al. · 2010 · arXiv:1005.2092
Source status unknown — claims are unverified
Hot isostatic pressing of bulk magnesium diboride: mechanical and superconducting properties
similarity 0.90S. S. Indrakanti et al. · 2001 · arXiv:cond-mat/0105485
Source status unknown — claims are unverified
High-pressure synthesis of MgB2 with addition of Ti
similarity 0.90T. A. Prikhna et al. · 2003 · arXiv:cond-mat/0306013
Source status unknown — claims are unverified
Microstructure and superconducting properties of hot isostatically pressed MgB2
similarity 0.90T C Shields et al. · 2001 · arXiv:cond-mat/0107034
Source status unknown — claims are unverified
Superconductivity in high-pressure synthesized pure and doped MgB2 compounds
similarity 0.89P. Toulemonde et al. · 2002 · arXiv:cond-mat/0206409
Source status unknown — claims are unverified
Positive influence of ta addition on superconductive properties of high pressure synthesized MgB_2
similarity 0.89T. Prikhna et al. · 2002 · arXiv:cond-mat/0204362
Source status unknown — claims are unverified