Effects of high pressure on the physical properties of MgB2
T. Prikhna, W. Gawalek, Ya. Savchuk, A. Soldatov, V. Sokolovsky, M. Eisterer, H. W. Weber, J. Noudem, M. Serga, V. Turkevich, M. Tompsic, V. Tkach, N. Danilenko, W. Goldacker, F. Karau, I. Fesenko, M. Rindfleisch, J. Dellith, M. Wendt, S. You, V. Meerovich, S. Dub, V. Moshchil, N. Sergienko, A. Kozyrev, T. Habisreuther, Ch. Schmidt, D. Litzkendorf, P. Nagorny, V. Sverdun
arXiv:1005.2092 · DOI 10.1007/S10948-010-0909-3 · 2010-05-12 · Journal of Superconductivity and Novel Magnetism
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and mechanical characteristics: critical current densities of 1.8-1.0 \cdot 106 A/cm2 in the self field and 103 A/cm2 in a magnetic field of 8 T at 20 K, 5-3 \cdot 105 A/cm2 in self field at 30 K, the corresponding critical fields being HC2 = 15 T at 22 K and irreversible fields Hirr =13 T at 20 K, and Hirr =3.5 T at 30 K, thermal conduction of 53+/-2 W/(m \cdot κ), the Vickers hardness Hv=10.12+/-0.2 GPa under a load of 148.8 N and the fracture toughness K1C = 7.6+/-2.0 MPa m0.5 under the same load, the Young modulus E=213 GPa. Estimation of quenching current and AC losses allowed the conclusion that highpressure-prepared materials are promising for application in transformer-type fault current limiters working at 20-30 K.
Similar papers
The high-pressure synthesis of MgB2
similarity 0.91T. A. Prikhna et al. · 2001 · arXiv:cond-mat/0109216
Source status unknown — claims are unverified
Positive influence of ta addition on superconductive properties of high pressure synthesized MgB_2
similarity 0.89T. Prikhna et al. · 2002 · arXiv:cond-mat/0204362
Source status unknown — claims are unverified
Synthesis and Sintering of MgB2 Under High Pressure
similarity 0.89T. A. Prikhna et al. · 2002 · arXiv:cond-mat/0204068
Source status unknown — claims are unverified
Bulk Magnesium Diboride, Mechanical and Superconducting Properties
similarity 0.89Vitali F. Nesterenko · 2002 · arXiv:cond-mat/0212543
Source status unknown — claims are unverified
Superconducting Properties of MgB2 Bulk Materials Prepared by High Pressure Sintering
similarity 0.89Y. Takano et al. · 2001 · arXiv:cond-mat/0102167
Source status unknown — claims are unverified
Temperature dependence of trapped magnetic field in MgB2 bulk superconductor
similarity 0.89R. V. Viznichenko et al. · 2003 · arXiv:cond-mat/0307318
Source status unknown — claims are unverified