Bulk Magnesium Diboride, Mechanical and Superconducting Properties
Vitali F. Nesterenko
arXiv:cond-mat/0212543 · 2002-12-21 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Hot Isostatic Pressing was applied to synthesize bulk samples with diameter up to 30 mm starting with Alfa Aesar magnesium diboride powder. HIPing at 2 kbar, 1000 C with cooling under pressure (DMCUP cycle) resulted in a fully dense (or low porosity) material with a sharp superconducting transition and critical current comparable with the best reported. Elastic constants were measured using method of resonant ultrasound spectroscopy. Their values for most dense samples (bulk modulus 142.5 GPa and Young's modulus 272.5 GPa) are close to theoretically predicted values for solid magnesium diboride. Porosity is resposible for lower values of elastic constants. Fracture toughness is evaluated based on measurements of microhardness and elastic constants. Upper critical field and irreversibility field are comparable with data for samples sintered at 3 GPa. Microstructural propeties of HIPed smaples are responsible for enhanced flux pinning. Method allows scaling of the size of the samples and manufacture of complex shapes.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Hot isostatic pressing of bulk magnesium diboride: mechanical and superconducting properties
similarity 0.94S. S. Indrakanti et al. · 2001 · arXiv:cond-mat/0105485
Source status unknown — claims are unverified
Microstructure and superconducting properties of hot isostatically pressed MgB2
similarity 0.91T C Shields et al. · 2001 · arXiv:cond-mat/0107034
Source status unknown — claims are unverified
The high gas pressure HIP influence on structure and transport properties of superconductors of single and multicore composition
similarity 0.91T. Cetner et al. · 2014 · arXiv:1406.2141
Source status unknown — claims are unverified
Effects of high pressure on the physical properties of MgB2
similarity 0.89T. Prikhna et al. · 2010 · arXiv:1005.2092
Source status unknown — claims are unverified
The high-pressure synthesis of MgB2
similarity 0.88T. A. Prikhna et al. · 2001 · arXiv:cond-mat/0109216
Source status unknown — claims are unverified
Improved superconducting properties of MgB2
similarity 0.88N. A. Frederick et al. · 2001 · arXiv:cond-mat/0106518
Source status unknown — claims are unverified