Hot isostatic pressing of bulk magnesium diboride: mechanical and superconducting properties
S. S. Indrakanti, V. F. Nesterenko, M. B. Maple, N. A. Frederick, W. M. Yuhasz, Shi Li
arXiv:cond-mat/0105485 · DOI 10.1080/09500830110093236 · 2001-05-24 · Philosophical Magazine Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Two different hot isostatic pressing cycles (HIPing) were investigated to synthesize bulk MgB2 samples: a "standard" cycle where a low vessel pressure is maintained while heating to the process temperature with a subsequent simultaneous pressure and temperature decrease and a new method - dense material cooling under pressure (DMCUP). The latter method allowed the synthesis of dense samples with diameters up to 20 mm and thicknesses up to 10 mm from commercial MgB2 powder. Optimal conditions for the DMCUP method with glass encapsulation (maximum pressure 200 MPa, maximum temperature 1000 C over 200 min, and cooling under pressure) resulted in a dense material with a sharp superconducting transition at 38.5 K. This method employs a pressure which is one order of magnitude less than previously reported for pressure assisted sintering of dense material and can be scaled to larger sample sizes and complex shapes. The data for density, microhardness, fracture toughness and sound speed as well as superconducting properties for bulk magnesium diboride are presented. Ball milling the powder enhances sintering and results in a more homogeneous final microstructure.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 38.5 | Pressure unresolved | unknown |
Similar papers
Bulk Magnesium Diboride, Mechanical and Superconducting Properties
similarity 0.94Vitali F. Nesterenko · 2002 · arXiv:cond-mat/0212543
Source status unknown — claims are unverified
Comparative Study of Dense Bulk MgB Materials Prepared by Different Methods
similarity 0.90V. N. Narozhnyi et al. · 2002 · arXiv:cond-mat/0206513
Source status unknown — claims are unverified
The high-pressure synthesis of MgB2
similarity 0.90T. A. Prikhna et al. · 2001 · arXiv:cond-mat/0109216
Source status unknown — claims are unverified
Temperature dependence of trapped magnetic field in MgB2 bulk superconductor
similarity 0.88R. V. Viznichenko et al. · 2003 · arXiv:cond-mat/0307318
Source status unknown — claims are unverified
Superconducting Properties of MgB2 Bulk Materials Prepared by High Pressure Sintering
similarity 0.88Y. Takano et al. · 2001 · arXiv:cond-mat/0102167
Source status unknown — claims are unverified
A Trapped Field of >3T in Bulk MgB2 Fabricated by Uniaxial Hot Pressing
similarity 0.87J. H. Durrell et al. · 2012 · arXiv:1207.6982
Source status unknown — claims are unverified