Superconducting Properties of MgB2 Bulk Materials Prepared by High Pressure Sintering
Y. Takano, H. Takeya, H. Fujii, H. Kumakura, T. Hatano, K. Togano, H. Kito, H. Ihara
arXiv:cond-mat/0102167 · DOI 10.1063/1.1371239 · 2001-02-09 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive measurements. Magnetization versus field (M-H) curve shows the behavior of a typical Type II superconductor and the lower critical field Hc1(0) estimated from M-H curve is 0.032T. The bulk sample shows good connection between grains and critical current density Jc estimated from the magnetization hysteresis using sample size was 2x104A/cm2 at 20K and 1T. Upper critical field Hc2(0) determined by extrapolating the onset of resistive transition and assuming a dirty limit is 18T.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39 | Pressure not reported | onset |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39 | Pressure not reported | onset |
Similar papers
Microstructure and superconducting properties of hot isostatically pressed MgB2
similarity 0.92T C Shields et al. · 2001 · arXiv:cond-mat/0107034
Source status unknown — claims are unverified
Comparative Study of Dense Bulk MgB Materials Prepared by Different Methods
similarity 0.91V. N. Narozhnyi et al. · 2002 · arXiv:cond-mat/0206513
Source status unknown — claims are unverified
Superconducting Properties of Combustion Synthesized MgB2
similarity 0.91Takano, Yoshihiko et al. · 2016 · arXiv:cond-mat/0401572
Source status unknown — claims are unverified
Superconducting Properties of Highly Dense MgB2 Bulk Materials
similarity 0.91G. Giunchi et al. · 2002 · arXiv:cond-mat/0208043
Source status unknown — claims are unverified
Effect of sintering temperature under high pressure in the uperconductivity for MgB2
similarity 0.90C. U. Jung et al. · 2001 · arXiv:cond-mat/0102383
Source status unknown — claims are unverified
Improved superconducting properties in nanocrystalline bulk MgB_2
similarity 0.90A. Gümbel et al. · 2001 · arXiv:cond-mat/0111585
Source status unknown — claims are unverified