T. Prikhna, W. Gawalek, N. Novikov, Ya. Savchuk, V. Moshchil, N. Sergienko, M. Wendt, S. Dub, V. Melnikov, A. Surzhenko, D. Litzkendorf, P. Nagorny, C. Schmidt
arXiv:cond-mat/0204362 · 2002-04-17 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Bulk MgB2 - based materials with the following critical current densities (jc) in 1 T field: 570 kA/cm^2 at 10 K, 350 kA/cm^2 at 20 K and 40 kA/cm^2 at 30 K and in 10 T field: 650 A/cm^2 at 10 K have been high-pressure (HP) synthesized from Mg and B with 2 - 10 wt.% addition of Ta. In synthesis and sintering process Ta plays the role of an absorbent of impurity gases (hydrogen, nitrogen, etc.) and forms Ta2H, TaH, TaN0.1, etc., thus promotes the reduction of MgH2 in Mg-B-O-matrix phase, as well as, the impurity nitrogen and oxygen in Mg-B grains (black MgB2 single crystals distributed over the matrix). Vickers microhardness of HP-synthesized material is Hv=12.54 (+/-)0.86 GPa (at 0.496-N load) The hardness (at 60-mN load) of MgB2 single crystals located in a sample matrix is 35.6 (+/-)0.9 GPa that is higher than the hardness of sapphire (31.1 (+/-)2.0 GPa).
Similar papers
Synthesis and Sintering of MgB2 Under High Pressure
similarity 0.94T. A. Prikhna et al. · 2002 · arXiv:cond-mat/0204068
Source status unknown — claims are unverified
High-pressure synthesis of MgB2 with addition of Ti
similarity 0.89T. A. Prikhna et al. · 2003 · arXiv:cond-mat/0306013
Source status unknown — claims are unverified
Effect of higher borides and inhomogeneity of oxygen distribution on critical current density of undoped and doped magnesium diboride
similarity 0.88T. A. Prikhna et al. · 2009 · arXiv:0912.4889
Source status unknown — claims are unverified
Physical Property Characterization of Bulk MgB2 Superconductor
similarity 0.86V. P. S. Awana et al. · 2008 · arXiv:0807.1203
Source status unknown — claims are unverified
Improved Current Densities in MgB2 By Liquid-Assisted Sintering
similarity 0.85S. K. Chen et al. · 2005 · arXiv:cond-mat/0504793
Source status unknown — claims are unverified
Enhanced critical current density of MgB2 superconductor synthesized in high magnetic fields
similarity 0.85Yanwei Ma et al. · 2006 · arXiv:cond-mat/0601245
Source status unknown — claims are unverified